Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state
- Autores
- Lopez, Carlos Alberto; Saleta, Martin Eduardo; Pedregosa, Jose Carmelo; Sanchez, Rodolfo Daniel; Lamas, Diego Germán; Alonso, J. A.; Fernández Díaz, M. T.
- Año de publicación
- 2016
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Sr3MnMo2O9 and Ba3MnMo2O9 double perovskites with Mo5+ valence states have been prepared in polycrystalline form by thermal treatment, in reducing atmosphere (H2/N2 flow), of previously decomposed citrate precursors. These materials have been studied by X-ray and neutron powder diffraction (XRPD, NPD), magnetic and transport measurements. At room temperature, the crystal structure of Sr3MnMo2O9 is monoclinic, space group P21/n, with a = 5.6564(1) Å, b = 5.6383(1) Å, c = 7.9765(2) Å, β = 89.994(7) whereas Ba3MnMo2O9 presents a cubic lattice, space group Fm3¯ m, with a = 8.14900(8) Å. These samples present a frustrated magnetic interaction below to 12 and 9 K for Sr3MnMo2O9 and Ba3MnMo2O9, respectively. Semiconductor behaviour, observed either from d.c. or a.c. measurements, was modelled by a variable-range hopping mechanism. This transport behaviour is in accord with the electronic configurations Mn2+(3 d5)-Mo5+(4 d1) and supports the absence of mixed valence states in both double perovkites.
Fil: Lopez, Carlos Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Saleta, Martin Eduardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Universidad Nacional de Cuyo; Argentina
Fil: Pedregosa, Jose Carmelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Sanchez, Rodolfo Daniel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Universidad Nacional de Cuyo; Argentina
Fil: Lamas, Diego Germán. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina
Fil: Alonso, J. A.. Instituto de Ciencia de Materiales de Madrid; España. Consejo Superior de Investigaciones Científicas; España
Fil: Fernández Díaz, M. T.. Institut Laue Langevin; Francia - Materia
-
CRYSTAL STRUCTURE
ELECTRONIC PROPERTIES
IMPEDANCE SPECTROSCOPY
INORGANIC MATERIALS
MAGNETIC MEASUREMENTS
NEUTRON DIFFRACTION - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/5819
Ver los metadatos del registro completo
id |
CONICETDig_d5ec718eaf233b8ab0f84237dfcd080e |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/5819 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence stateLopez, Carlos AlbertoSaleta, Martin EduardoPedregosa, Jose CarmeloSanchez, Rodolfo DanielLamas, Diego GermánAlonso, J. A.Fernández Díaz, M. T.CRYSTAL STRUCTUREELECTRONIC PROPERTIESIMPEDANCE SPECTROSCOPYINORGANIC MATERIALSMAGNETIC MEASUREMENTSNEUTRON DIFFRACTIONhttps://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1Sr3MnMo2O9 and Ba3MnMo2O9 double perovskites with Mo5+ valence states have been prepared in polycrystalline form by thermal treatment, in reducing atmosphere (H2/N2 flow), of previously decomposed citrate precursors. These materials have been studied by X-ray and neutron powder diffraction (XRPD, NPD), magnetic and transport measurements. At room temperature, the crystal structure of Sr3MnMo2O9 is monoclinic, space group P21/n, with a = 5.6564(1) Å, b = 5.6383(1) Å, c = 7.9765(2) Å, β = 89.994(7) whereas Ba3MnMo2O9 presents a cubic lattice, space group Fm3¯ m, with a = 8.14900(8) Å. These samples present a frustrated magnetic interaction below to 12 and 9 K for Sr3MnMo2O9 and Ba3MnMo2O9, respectively. Semiconductor behaviour, observed either from d.c. or a.c. measurements, was modelled by a variable-range hopping mechanism. This transport behaviour is in accord with the electronic configurations Mn2+(3 d5)-Mo5+(4 d1) and supports the absence of mixed valence states in both double perovkites.Fil: Lopez, Carlos Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Saleta, Martin Eduardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Universidad Nacional de Cuyo; ArgentinaFil: Pedregosa, Jose Carmelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Sanchez, Rodolfo Daniel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Universidad Nacional de Cuyo; ArgentinaFil: Lamas, Diego Germán. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; ArgentinaFil: Alonso, J. A.. Instituto de Ciencia de Materiales de Madrid; España. Consejo Superior de Investigaciones Científicas; EspañaFil: Fernández Díaz, M. T.. Institut Laue Langevin; FranciaElsevier Science Sa2016-03info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/5819Lopez, Carlos Alberto; Saleta, Martin Eduardo; Pedregosa, Jose Carmelo; Sanchez, Rodolfo Daniel; Lamas, Diego Germán; et al.; Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state; Elsevier Science Sa; Journal of Alloys and Compounds; 661; 3-2016; 411-4180925-8388enginfo:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0925838815317618info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jallcom.2015.11.204info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:33:19Zoai:ri.conicet.gov.ar:11336/5819instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:33:20.112CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
title |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
spellingShingle |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state Lopez, Carlos Alberto CRYSTAL STRUCTURE ELECTRONIC PROPERTIES IMPEDANCE SPECTROSCOPY INORGANIC MATERIALS MAGNETIC MEASUREMENTS NEUTRON DIFFRACTION |
title_short |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
title_full |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
title_fullStr |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
title_full_unstemmed |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
title_sort |
Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state |
dc.creator.none.fl_str_mv |
Lopez, Carlos Alberto Saleta, Martin Eduardo Pedregosa, Jose Carmelo Sanchez, Rodolfo Daniel Lamas, Diego Germán Alonso, J. A. Fernández Díaz, M. T. |
author |
Lopez, Carlos Alberto |
author_facet |
Lopez, Carlos Alberto Saleta, Martin Eduardo Pedregosa, Jose Carmelo Sanchez, Rodolfo Daniel Lamas, Diego Germán Alonso, J. A. Fernández Díaz, M. T. |
author_role |
author |
author2 |
Saleta, Martin Eduardo Pedregosa, Jose Carmelo Sanchez, Rodolfo Daniel Lamas, Diego Germán Alonso, J. A. Fernández Díaz, M. T. |
author2_role |
author author author author author author |
dc.subject.none.fl_str_mv |
CRYSTAL STRUCTURE ELECTRONIC PROPERTIES IMPEDANCE SPECTROSCOPY INORGANIC MATERIALS MAGNETIC MEASUREMENTS NEUTRON DIFFRACTION |
topic |
CRYSTAL STRUCTURE ELECTRONIC PROPERTIES IMPEDANCE SPECTROSCOPY INORGANIC MATERIALS MAGNETIC MEASUREMENTS NEUTRON DIFFRACTION |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/1.4 https://purl.org/becyt/ford/1 |
dc.description.none.fl_txt_mv |
Sr3MnMo2O9 and Ba3MnMo2O9 double perovskites with Mo5+ valence states have been prepared in polycrystalline form by thermal treatment, in reducing atmosphere (H2/N2 flow), of previously decomposed citrate precursors. These materials have been studied by X-ray and neutron powder diffraction (XRPD, NPD), magnetic and transport measurements. At room temperature, the crystal structure of Sr3MnMo2O9 is monoclinic, space group P21/n, with a = 5.6564(1) Å, b = 5.6383(1) Å, c = 7.9765(2) Å, β = 89.994(7) whereas Ba3MnMo2O9 presents a cubic lattice, space group Fm3¯ m, with a = 8.14900(8) Å. These samples present a frustrated magnetic interaction below to 12 and 9 K for Sr3MnMo2O9 and Ba3MnMo2O9, respectively. Semiconductor behaviour, observed either from d.c. or a.c. measurements, was modelled by a variable-range hopping mechanism. This transport behaviour is in accord with the electronic configurations Mn2+(3 d5)-Mo5+(4 d1) and supports the absence of mixed valence states in both double perovkites. Fil: Lopez, Carlos Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina Fil: Saleta, Martin Eduardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Universidad Nacional de Cuyo; Argentina Fil: Pedregosa, Jose Carmelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina Fil: Sanchez, Rodolfo Daniel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area de Investigación y Aplicaciones No Nucleares. Gerencia de Física. Laboratorio de Resonancias Magnéticas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Universidad Nacional de Cuyo; Argentina Fil: Lamas, Diego Germán. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de San Martín. Escuela de Ciencia y Tecnología; Argentina Fil: Alonso, J. A.. Instituto de Ciencia de Materiales de Madrid; España. Consejo Superior de Investigaciones Científicas; España Fil: Fernández Díaz, M. T.. Institut Laue Langevin; Francia |
description |
Sr3MnMo2O9 and Ba3MnMo2O9 double perovskites with Mo5+ valence states have been prepared in polycrystalline form by thermal treatment, in reducing atmosphere (H2/N2 flow), of previously decomposed citrate precursors. These materials have been studied by X-ray and neutron powder diffraction (XRPD, NPD), magnetic and transport measurements. At room temperature, the crystal structure of Sr3MnMo2O9 is monoclinic, space group P21/n, with a = 5.6564(1) Å, b = 5.6383(1) Å, c = 7.9765(2) Å, β = 89.994(7) whereas Ba3MnMo2O9 presents a cubic lattice, space group Fm3¯ m, with a = 8.14900(8) Å. These samples present a frustrated magnetic interaction below to 12 and 9 K for Sr3MnMo2O9 and Ba3MnMo2O9, respectively. Semiconductor behaviour, observed either from d.c. or a.c. measurements, was modelled by a variable-range hopping mechanism. This transport behaviour is in accord with the electronic configurations Mn2+(3 d5)-Mo5+(4 d1) and supports the absence of mixed valence states in both double perovkites. |
publishDate |
2016 |
dc.date.none.fl_str_mv |
2016-03 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/5819 Lopez, Carlos Alberto; Saleta, Martin Eduardo; Pedregosa, Jose Carmelo; Sanchez, Rodolfo Daniel; Lamas, Diego Germán; et al.; Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state; Elsevier Science Sa; Journal of Alloys and Compounds; 661; 3-2016; 411-418 0925-8388 |
url |
http://hdl.handle.net/11336/5819 |
identifier_str_mv |
Lopez, Carlos Alberto; Saleta, Martin Eduardo; Pedregosa, Jose Carmelo; Sanchez, Rodolfo Daniel; Lamas, Diego Germán; et al.; Electronic properties in intrinsically disordered double perovskites: Sr3MnMo2O9 and Ba3MnMo2O9 with Mo5+ valence state; Elsevier Science Sa; Journal of Alloys and Compounds; 661; 3-2016; 411-418 0925-8388 |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0925838815317618 info:eu-repo/semantics/altIdentifier/doi/10.1016/j.jallcom.2015.11.204 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier Science Sa |
publisher.none.fl_str_mv |
Elsevier Science Sa |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613023229018112 |
score |
13.070432 |