Descripción
We report on the influence of random point defects introduced by 3 MeV proton irradiation on the vortex dynamics of 1.3 μm thick GdBa2Cu3Ox coated conductors. Thin films with different oxygen stoichiometry (6.7 < × < 7) were irradiated with 3 MeV proton (p) using a fluence of 2 × 1016 p cm−2. We find a direct correlation between the changes in Tc produced by oxygen content and damage by irradiation on the resulting vortex dynamics in the films. The analysis of the critical current densities Jc at low temperatures indicates that although irradiation produces smooth magnetic field dependences, the self-field values decrease systematically as Tc reduces. Moreover, the analysis of the relaxation of the persistent currents shows that the characteristic glassy exponent μ systematically decreases from 1.7 to 0.66 as Tc decreases from 93 to 55 K.
Fil: Haberkorn, Nestor Fabian. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; Argentina
Fil: Guimpel, Julio Juan. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; Argentina
Fil: Suárez, S.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Comisión Nacional de Energía Atómica; Argentina
Fil: Lee, Jae-Hun. No especifíca;
Fil: Lee, Hunju. No especifíca;
Fil: Moon, S.H.. No especifíca;
Materia
COATED CONDUCTORS
OXYGEN STOICHIOMETRY
PROTON IRRADIATION
VORTEX DYNAMICS
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/123733
Acceder
id CONICETDig_c6b9614b0902b01ef2fa5bf295ea4e51
oai_identifier_str oai:ri.conicet.gov.ar:11336/123733
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductorsHaberkorn, Nestor FabianGuimpel, Julio JuanSuárez, S.Lee, Jae-HunLee, HunjuMoon, S.H.COATED CONDUCTORSOXYGEN STOICHIOMETRYPROTON IRRADIATIONVORTEX DYNAMICShttps://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1We report on the influence of random point defects introduced by 3 MeV proton irradiation on the vortex dynamics of 1.3 μm thick GdBa2Cu3Ox coated conductors. Thin films with different oxygen stoichiometry (6.7 < × < 7) were irradiated with 3 MeV proton (p) using a fluence of 2 × 1016 p cm−2. We find a direct correlation between the changes in Tc produced by oxygen content and damage by irradiation on the resulting vortex dynamics in the films. The analysis of the critical current densities Jc at low temperatures indicates that although irradiation produces smooth magnetic field dependences, the self-field values decrease systematically as Tc reduces. Moreover, the analysis of the relaxation of the persistent currents shows that the characteristic glassy exponent μ systematically decreases from 1.7 to 0.66 as Tc decreases from 93 to 55 K.Fil: Haberkorn, Nestor Fabian. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; ArgentinaFil: Guimpel, Julio Juan. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; ArgentinaFil: Suárez, S.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Comisión Nacional de Energía Atómica; ArgentinaFil: Lee, Jae-Hun. No especifíca;Fil: Lee, Hunju. No especifíca;Fil: Moon, S.H.. No especifíca;IOP Publishing2019-11info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/123733Haberkorn, Nestor Fabian; Guimpel, Julio Juan; Suárez, S.; Lee, Jae-Hun; Lee, Hunju; et al.; Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors; IOP Publishing; Superconductor Science And Technology; 32; 12; 11-2019; 1-70953-2048CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1088/1361-6668/ab5164info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:03:44Zoai:ri.conicet.gov.ar:11336/123733instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:03:44.465CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
title Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
spellingShingle Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
Haberkorn, Nestor Fabian
COATED CONDUCTORS
OXYGEN STOICHIOMETRY
PROTON IRRADIATION
VORTEX DYNAMICS
title_short Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
title_full Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
title_fullStr Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
title_full_unstemmed Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
title_sort Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors
dc.creator.none.fl_str_mv Haberkorn, Nestor Fabian
Guimpel, Julio Juan
Suárez, S.
Lee, Jae-Hun
Lee, Hunju
Moon, S.H.
author Haberkorn, Nestor Fabian
author_facet Haberkorn, Nestor Fabian
Guimpel, Julio Juan
Suárez, S.
Lee, Jae-Hun
Lee, Hunju
Moon, S.H.
author_role author
author2 Guimpel, Julio Juan
Suárez, S.
Lee, Jae-Hun
Lee, Hunju
Moon, S.H.
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv COATED CONDUCTORS
OXYGEN STOICHIOMETRY
PROTON IRRADIATION
VORTEX DYNAMICS
topic COATED CONDUCTORS
OXYGEN STOICHIOMETRY
PROTON IRRADIATION
VORTEX DYNAMICS
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.3
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv We report on the influence of random point defects introduced by 3 MeV proton irradiation on the vortex dynamics of 1.3 μm thick GdBa2Cu3Ox coated conductors. Thin films with different oxygen stoichiometry (6.7 < × < 7) were irradiated with 3 MeV proton (p) using a fluence of 2 × 1016 p cm−2. We find a direct correlation between the changes in Tc produced by oxygen content and damage by irradiation on the resulting vortex dynamics in the films. The analysis of the critical current densities Jc at low temperatures indicates that although irradiation produces smooth magnetic field dependences, the self-field values decrease systematically as Tc reduces. Moreover, the analysis of the relaxation of the persistent currents shows that the characteristic glassy exponent μ systematically decreases from 1.7 to 0.66 as Tc decreases from 93 to 55 K.
Fil: Haberkorn, Nestor Fabian. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; Argentina
Fil: Guimpel, Julio Juan. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche | Comisión Nacional de Energía Atómica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología. Unidad Ejecutora Instituto de Nanociencia y Nanotecnología - Nodo Bariloche; Argentina
Fil: Suárez, S.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina. Comisión Nacional de Energía Atómica; Argentina
Fil: Lee, Jae-Hun. No especifíca;
Fil: Lee, Hunju. No especifíca;
Fil: Moon, S.H.. No especifíca;
description We report on the influence of random point defects introduced by 3 MeV proton irradiation on the vortex dynamics of 1.3 μm thick GdBa2Cu3Ox coated conductors. Thin films with different oxygen stoichiometry (6.7 < × < 7) were irradiated with 3 MeV proton (p) using a fluence of 2 × 1016 p cm−2. We find a direct correlation between the changes in Tc produced by oxygen content and damage by irradiation on the resulting vortex dynamics in the films. The analysis of the critical current densities Jc at low temperatures indicates that although irradiation produces smooth magnetic field dependences, the self-field values decrease systematically as Tc reduces. Moreover, the analysis of the relaxation of the persistent currents shows that the characteristic glassy exponent μ systematically decreases from 1.7 to 0.66 as Tc decreases from 93 to 55 K.
publishDate 2019
dc.date.none.fl_str_mv 2019-11
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/123733
Haberkorn, Nestor Fabian; Guimpel, Julio Juan; Suárez, S.; Lee, Jae-Hun; Lee, Hunju; et al.; Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors; IOP Publishing; Superconductor Science And Technology; 32; 12; 11-2019; 1-7
0953-2048
CONICET Digital
CONICET
url http://hdl.handle.net/11336/123733
identifier_str_mv Haberkorn, Nestor Fabian; Guimpel, Julio Juan; Suárez, S.; Lee, Jae-Hun; Lee, Hunju; et al.; Competition between pinning produced by extrinsic random point disorder and superconducting thermal fluctuations in oxygen-deficient GdBa2Cu3Ox coated conductors; IOP Publishing; Superconductor Science And Technology; 32; 12; 11-2019; 1-7
0953-2048
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1088/1361-6668/ab5164
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv IOP Publishing
publisher.none.fl_str_mv IOP Publishing
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844613856827015168
score 13.070432

Publicaciones similares