A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides

Autores
Morris, W.; Vazquez, Marcela Vivian
Año de publicación
2002
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
The performance of a surface-applied migrating corrosion inhibitor (MCI) based on an alkylaminoalcohol was evaluated on concrete specimens containing reinforcing steel bar (rebar) segments. Two water/cement ratios (w/c's), various chloride contents and two exposure conditions were investigated. The inhibiting efficiency was followed over a period of 1000 days by means of parameters such as corrosion potential, corrosion current and electrical resistance. Results show that when concrete is exposed to the marine environment, the inhibitor is able to reduce the corrosion rate (CR) only when the initial chloride content is below 0.16 wt.% relative to cement content. Efficiency increases as the w/c increases. There is no beneficial effect when the initial chloride content is greater than 0.43%. When concrete is immersed in a saline solution, no beneficial effect associated to the use of the inhibitor could be appreciated, regardless of w/c or initial chloride content in concrete.
Fil: Morris, W.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Vazquez, Marcela Vivian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Materia
Chloride
Corrosion
Durability
Electrochemical Properties
Inhibitors
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/53925
Acceder
id CONICETDig_c4ba03566933b9da1f3efa6d9412c5ee
oai_identifier_str oai:ri.conicet.gov.ar:11336/53925
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chloridesMorris, W.Vazquez, Marcela VivianChlorideCorrosionDurabilityElectrochemical PropertiesInhibitorshttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2The performance of a surface-applied migrating corrosion inhibitor (MCI) based on an alkylaminoalcohol was evaluated on concrete specimens containing reinforcing steel bar (rebar) segments. Two water/cement ratios (w/c's), various chloride contents and two exposure conditions were investigated. The inhibiting efficiency was followed over a period of 1000 days by means of parameters such as corrosion potential, corrosion current and electrical resistance. Results show that when concrete is exposed to the marine environment, the inhibitor is able to reduce the corrosion rate (CR) only when the initial chloride content is below 0.16 wt.% relative to cement content. Efficiency increases as the w/c increases. There is no beneficial effect when the initial chloride content is greater than 0.43%. When concrete is immersed in a saline solution, no beneficial effect associated to the use of the inhibitor could be appreciated, regardless of w/c or initial chloride content in concrete.Fil: Morris, W.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Vazquez, Marcela Vivian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaPergamon-Elsevier Science Ltd2002-02info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/53925Morris, W.; Vazquez, Marcela Vivian; A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides; Pergamon-Elsevier Science Ltd; Cement and Concrete Research; 32; 2; 2-2002; 259-2670008-8846CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/S0008-8846(01)00669-Xinfo:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S000888460100669Xinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-15T15:00:00Zoai:ri.conicet.gov.ar:11336/53925instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-15 15:00:00.396CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
title A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
spellingShingle A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
Morris, W.
Chloride
Corrosion
Durability
Electrochemical Properties
Inhibitors
title_short A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
title_full A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
title_fullStr A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
title_full_unstemmed A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
title_sort A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides
dc.creator.none.fl_str_mv Morris, W.
Vazquez, Marcela Vivian
author Morris, W.
author_facet Morris, W.
Vazquez, Marcela Vivian
author_role author
author2 Vazquez, Marcela Vivian
author2_role author
dc.subject.none.fl_str_mv Chloride
Corrosion
Durability
Electrochemical Properties
Inhibitors
topic Chloride
Corrosion
Durability
Electrochemical Properties
Inhibitors
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv The performance of a surface-applied migrating corrosion inhibitor (MCI) based on an alkylaminoalcohol was evaluated on concrete specimens containing reinforcing steel bar (rebar) segments. Two water/cement ratios (w/c's), various chloride contents and two exposure conditions were investigated. The inhibiting efficiency was followed over a period of 1000 days by means of parameters such as corrosion potential, corrosion current and electrical resistance. Results show that when concrete is exposed to the marine environment, the inhibitor is able to reduce the corrosion rate (CR) only when the initial chloride content is below 0.16 wt.% relative to cement content. Efficiency increases as the w/c increases. There is no beneficial effect when the initial chloride content is greater than 0.43%. When concrete is immersed in a saline solution, no beneficial effect associated to the use of the inhibitor could be appreciated, regardless of w/c or initial chloride content in concrete.
Fil: Morris, W.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Vazquez, Marcela Vivian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
description The performance of a surface-applied migrating corrosion inhibitor (MCI) based on an alkylaminoalcohol was evaluated on concrete specimens containing reinforcing steel bar (rebar) segments. Two water/cement ratios (w/c's), various chloride contents and two exposure conditions were investigated. The inhibiting efficiency was followed over a period of 1000 days by means of parameters such as corrosion potential, corrosion current and electrical resistance. Results show that when concrete is exposed to the marine environment, the inhibitor is able to reduce the corrosion rate (CR) only when the initial chloride content is below 0.16 wt.% relative to cement content. Efficiency increases as the w/c increases. There is no beneficial effect when the initial chloride content is greater than 0.43%. When concrete is immersed in a saline solution, no beneficial effect associated to the use of the inhibitor could be appreciated, regardless of w/c or initial chloride content in concrete.
publishDate 2002
dc.date.none.fl_str_mv 2002-02
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/53925
Morris, W.; Vazquez, Marcela Vivian; A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides; Pergamon-Elsevier Science Ltd; Cement and Concrete Research; 32; 2; 2-2002; 259-267
0008-8846
CONICET Digital
CONICET
url http://hdl.handle.net/11336/53925
identifier_str_mv Morris, W.; Vazquez, Marcela Vivian; A migrating corrosion inhibitor evaluated in concrete containing various contents of admixed chlorides; Pergamon-Elsevier Science Ltd; Cement and Concrete Research; 32; 2; 2-2002; 259-267
0008-8846
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/S0008-8846(01)00669-X
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S000888460100669X
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Pergamon-Elsevier Science Ltd
publisher.none.fl_str_mv Pergamon-Elsevier Science Ltd
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846083138926673920
score 13.22299

Publicaciones similares