Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties

Autores
Hernández, Maria Florencia; Lopez, Paula Virginia; Violini, María Agustina; Suarez, Gustavo; Conconi, María Susana; Rendtorff Birrer, Nicolás Maximiliano
Año de publicación
2020
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
A processing strategy for obtaining alumina-spodumene ceramics from fine commercial powders is presented. In this work, a spodumene addition to calcined alumina powder was performed and their proportion was explored between 15 and 45 wt%. The industrial spodumene presented secondary phases, mainly albite and quartz. Mechanical properties were evaluated. Although they were lower than those of sintered alumina, based on the achieved values an adequate behavior in structural applications can be assumed, especially taking into account that the better mechanical behavior was coupled with the lower thermal expansion. Relatively low thermal expansion≈ (5 x 10-1 °C-1) behaviors were observed in one of the developed materials. Noncrystalline phases containing lithium were detected. We assume that all the lithium oxide incorporated through the spodumene is in the glassy phase after the sintering of the materials. This difference in lithium concentration in the composition of the resulting glass affected the thermal expansion of the developed materials. Particularly with low lithium content (30 wt% of additive) the material performance was enhanced. This, together with the mechanical behavior, encourages structural applications with high thermomechanical solicitations. With the information gathered, a wide range of materials with specific properties can be obtained by modulating the spodumene-alumina proportion only.
Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Lopez, Paula Virginia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Violini, María Agustina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Materia
ALUMINA
PROCESSING
SPODUMENE
STRUCTURAL CERAMICS
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/164951
Acceder
id CONICETDig_b84265428080f80e56a20e01bae289c7
oai_identifier_str oai:ri.conicet.gov.ar:11336/164951
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and propertiesHernández, Maria FlorenciaLopez, Paula VirginiaViolini, María AgustinaSuarez, GustavoConconi, María SusanaRendtorff Birrer, Nicolás MaximilianoALUMINAPROCESSINGSPODUMENESTRUCTURAL CERAMICShttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2A processing strategy for obtaining alumina-spodumene ceramics from fine commercial powders is presented. In this work, a spodumene addition to calcined alumina powder was performed and their proportion was explored between 15 and 45 wt%. The industrial spodumene presented secondary phases, mainly albite and quartz. Mechanical properties were evaluated. Although they were lower than those of sintered alumina, based on the achieved values an adequate behavior in structural applications can be assumed, especially taking into account that the better mechanical behavior was coupled with the lower thermal expansion. Relatively low thermal expansion≈ (5 x 10-1 °C-1) behaviors were observed in one of the developed materials. Noncrystalline phases containing lithium were detected. We assume that all the lithium oxide incorporated through the spodumene is in the glassy phase after the sintering of the materials. This difference in lithium concentration in the composition of the resulting glass affected the thermal expansion of the developed materials. Particularly with low lithium content (30 wt% of additive) the material performance was enhanced. This, together with the mechanical behavior, encourages structural applications with high thermomechanical solicitations. With the information gathered, a wide range of materials with specific properties can be obtained by modulating the spodumene-alumina proportion only.Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Lopez, Paula Virginia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Violini, María Agustina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaInt Inst Science Sintering (i I S S)2020-05info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/164951Hernández, Maria Florencia; Lopez, Paula Virginia; Violini, María Agustina; Suarez, Gustavo; Conconi, María Susana; et al.; Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties; Int Inst Science Sintering (i I S S); Science Of Sintering; 51; 4; 5-2020; 445-4580350-820XCONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1904445Hinfo:eu-repo/semantics/altIdentifier/doi/10.2298/SOS1904445Hinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-10T13:10:46Zoai:ri.conicet.gov.ar:11336/164951instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-10 13:10:46.266CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
title Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
spellingShingle Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
Hernández, Maria Florencia
ALUMINA
PROCESSING
SPODUMENE
STRUCTURAL CERAMICS
title_short Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
title_full Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
title_fullStr Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
title_full_unstemmed Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
title_sort Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties
dc.creator.none.fl_str_mv Hernández, Maria Florencia
Lopez, Paula Virginia
Violini, María Agustina
Suarez, Gustavo
Conconi, María Susana
Rendtorff Birrer, Nicolás Maximiliano
author Hernández, Maria Florencia
author_facet Hernández, Maria Florencia
Lopez, Paula Virginia
Violini, María Agustina
Suarez, Gustavo
Conconi, María Susana
Rendtorff Birrer, Nicolás Maximiliano
author_role author
author2 Lopez, Paula Virginia
Violini, María Agustina
Suarez, Gustavo
Conconi, María Susana
Rendtorff Birrer, Nicolás Maximiliano
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv ALUMINA
PROCESSING
SPODUMENE
STRUCTURAL CERAMICS
topic ALUMINA
PROCESSING
SPODUMENE
STRUCTURAL CERAMICS
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv A processing strategy for obtaining alumina-spodumene ceramics from fine commercial powders is presented. In this work, a spodumene addition to calcined alumina powder was performed and their proportion was explored between 15 and 45 wt%. The industrial spodumene presented secondary phases, mainly albite and quartz. Mechanical properties were evaluated. Although they were lower than those of sintered alumina, based on the achieved values an adequate behavior in structural applications can be assumed, especially taking into account that the better mechanical behavior was coupled with the lower thermal expansion. Relatively low thermal expansion≈ (5 x 10-1 °C-1) behaviors were observed in one of the developed materials. Noncrystalline phases containing lithium were detected. We assume that all the lithium oxide incorporated through the spodumene is in the glassy phase after the sintering of the materials. This difference in lithium concentration in the composition of the resulting glass affected the thermal expansion of the developed materials. Particularly with low lithium content (30 wt% of additive) the material performance was enhanced. This, together with the mechanical behavior, encourages structural applications with high thermomechanical solicitations. With the information gathered, a wide range of materials with specific properties can be obtained by modulating the spodumene-alumina proportion only.
Fil: Hernández, Maria Florencia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Lopez, Paula Virginia. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Violini, María Agustina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Suarez, Gustavo. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Conconi, María Susana. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
description A processing strategy for obtaining alumina-spodumene ceramics from fine commercial powders is presented. In this work, a spodumene addition to calcined alumina powder was performed and their proportion was explored between 15 and 45 wt%. The industrial spodumene presented secondary phases, mainly albite and quartz. Mechanical properties were evaluated. Although they were lower than those of sintered alumina, based on the achieved values an adequate behavior in structural applications can be assumed, especially taking into account that the better mechanical behavior was coupled with the lower thermal expansion. Relatively low thermal expansion≈ (5 x 10-1 °C-1) behaviors were observed in one of the developed materials. Noncrystalline phases containing lithium were detected. We assume that all the lithium oxide incorporated through the spodumene is in the glassy phase after the sintering of the materials. This difference in lithium concentration in the composition of the resulting glass affected the thermal expansion of the developed materials. Particularly with low lithium content (30 wt% of additive) the material performance was enhanced. This, together with the mechanical behavior, encourages structural applications with high thermomechanical solicitations. With the information gathered, a wide range of materials with specific properties can be obtained by modulating the spodumene-alumina proportion only.
publishDate 2020
dc.date.none.fl_str_mv 2020-05
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/164951
Hernández, Maria Florencia; Lopez, Paula Virginia; Violini, María Agustina; Suarez, Gustavo; Conconi, María Susana; et al.; Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties; Int Inst Science Sintering (i I S S); Science Of Sintering; 51; 4; 5-2020; 445-458
0350-820X
CONICET Digital
CONICET
url http://hdl.handle.net/11336/164951
identifier_str_mv Hernández, Maria Florencia; Lopez, Paula Virginia; Violini, María Agustina; Suarez, Gustavo; Conconi, María Susana; et al.; Dense alumina-mullite composite ceramics from alumina and spodumene-albite feldspar binary mixtures: Processing and properties; Int Inst Science Sintering (i I S S); Science Of Sintering; 51; 4; 5-2020; 445-458
0350-820X
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://www.doiserbia.nb.rs/Article.aspx?ID=0350-820X1904445H
info:eu-repo/semantics/altIdentifier/doi/10.2298/SOS1904445H
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Int Inst Science Sintering (i I S S)
publisher.none.fl_str_mv Int Inst Science Sintering (i I S S)
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842980545414299648
score 12.993085

Publicaciones similares