Integrity and service life of LPG carafes
- Autores
- Fazzini, Pablo Gabriel; Santi, O.; Belmonte, Juan Carlos; Otegui, Luis Jose
- Año de publicación
- 2002
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- The reliability of 10 kg liquefied petroleum gas carafes used nowadays in Argentine households is evaluated in this study. Chemical, mechanical and metallographic studies were performed to determine base metal, weld metal and heat affected zone conditions. Residual stresses were measured in both inner and outer surfaces of the carafes. Lower bound values of fracture toughness (K1C) were determined from upper shelf Charpy energy (CVN). Charpy tests at 0 °C were carried out. A marked increase in toughness of the base plate was found, as the date of fabrication increases. Diverse degrees of non-conformities, resulting in significant defects usually undetectable by external inspection, were found in the circumferential welds of 25% of all carafes manufactured before 1990. The number and criticality of these defects falls markedly in the carafes built after 1990. Serious errors during reconditioning, such as repairs of leaks and scratches, are indicative of a poor approach to the rehabilitation of the vessels. It is recommended to evaluate changes in the rehabilitation procedures and standards. A gradual process of substitution of the carafes built prior to 1990 is also recommended. © 2002 Elsevier Science Ltd. All rights reserved.
Fil: Fazzini, Pablo Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Santi, O.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Belmonte, Juan Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Otegui, Luis Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina - Materia
-
Household Carafes
Liquefied Petroleum Gas
Reliability
Weld Defects - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/54131
Ver los metadatos del registro completo
id |
CONICETDig_b7f4eb7cd7fcad4e881bb4f7d4532414 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/54131 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Integrity and service life of LPG carafesFazzini, Pablo GabrielSanti, O.Belmonte, Juan CarlosOtegui, Luis JoseHousehold CarafesLiquefied Petroleum GasReliabilityWeld Defectshttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2https://purl.org/becyt/ford/2.3https://purl.org/becyt/ford/2The reliability of 10 kg liquefied petroleum gas carafes used nowadays in Argentine households is evaluated in this study. Chemical, mechanical and metallographic studies were performed to determine base metal, weld metal and heat affected zone conditions. Residual stresses were measured in both inner and outer surfaces of the carafes. Lower bound values of fracture toughness (K1C) were determined from upper shelf Charpy energy (CVN). Charpy tests at 0 °C were carried out. A marked increase in toughness of the base plate was found, as the date of fabrication increases. Diverse degrees of non-conformities, resulting in significant defects usually undetectable by external inspection, were found in the circumferential welds of 25% of all carafes manufactured before 1990. The number and criticality of these defects falls markedly in the carafes built after 1990. Serious errors during reconditioning, such as repairs of leaks and scratches, are indicative of a poor approach to the rehabilitation of the vessels. It is recommended to evaluate changes in the rehabilitation procedures and standards. A gradual process of substitution of the carafes built prior to 1990 is also recommended. © 2002 Elsevier Science Ltd. All rights reserved.Fil: Fazzini, Pablo Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Santi, O.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Belmonte, Juan Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Otegui, Luis Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaElsevier2002-11info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/54131Fazzini, Pablo Gabriel; Santi, O.; Belmonte, Juan Carlos; Otegui, Luis Jose; Integrity and service life of LPG carafes; Elsevier; International Journal of Pressure Vessels and Piping; 79; 11; 11-2002; 767-7750308-0161CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/S0308-0161(02)00010-8info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0308016102000108info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:43:04Zoai:ri.conicet.gov.ar:11336/54131instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:43:04.331CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Integrity and service life of LPG carafes |
title |
Integrity and service life of LPG carafes |
spellingShingle |
Integrity and service life of LPG carafes Fazzini, Pablo Gabriel Household Carafes Liquefied Petroleum Gas Reliability Weld Defects |
title_short |
Integrity and service life of LPG carafes |
title_full |
Integrity and service life of LPG carafes |
title_fullStr |
Integrity and service life of LPG carafes |
title_full_unstemmed |
Integrity and service life of LPG carafes |
title_sort |
Integrity and service life of LPG carafes |
dc.creator.none.fl_str_mv |
Fazzini, Pablo Gabriel Santi, O. Belmonte, Juan Carlos Otegui, Luis Jose |
author |
Fazzini, Pablo Gabriel |
author_facet |
Fazzini, Pablo Gabriel Santi, O. Belmonte, Juan Carlos Otegui, Luis Jose |
author_role |
author |
author2 |
Santi, O. Belmonte, Juan Carlos Otegui, Luis Jose |
author2_role |
author author author |
dc.subject.none.fl_str_mv |
Household Carafes Liquefied Petroleum Gas Reliability Weld Defects |
topic |
Household Carafes Liquefied Petroleum Gas Reliability Weld Defects |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 https://purl.org/becyt/ford/2.3 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
The reliability of 10 kg liquefied petroleum gas carafes used nowadays in Argentine households is evaluated in this study. Chemical, mechanical and metallographic studies were performed to determine base metal, weld metal and heat affected zone conditions. Residual stresses were measured in both inner and outer surfaces of the carafes. Lower bound values of fracture toughness (K1C) were determined from upper shelf Charpy energy (CVN). Charpy tests at 0 °C were carried out. A marked increase in toughness of the base plate was found, as the date of fabrication increases. Diverse degrees of non-conformities, resulting in significant defects usually undetectable by external inspection, were found in the circumferential welds of 25% of all carafes manufactured before 1990. The number and criticality of these defects falls markedly in the carafes built after 1990. Serious errors during reconditioning, such as repairs of leaks and scratches, are indicative of a poor approach to the rehabilitation of the vessels. It is recommended to evaluate changes in the rehabilitation procedures and standards. A gradual process of substitution of the carafes built prior to 1990 is also recommended. © 2002 Elsevier Science Ltd. All rights reserved. Fil: Fazzini, Pablo Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Santi, O.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Belmonte, Juan Carlos. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina Fil: Otegui, Luis Jose. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina |
description |
The reliability of 10 kg liquefied petroleum gas carafes used nowadays in Argentine households is evaluated in this study. Chemical, mechanical and metallographic studies were performed to determine base metal, weld metal and heat affected zone conditions. Residual stresses were measured in both inner and outer surfaces of the carafes. Lower bound values of fracture toughness (K1C) were determined from upper shelf Charpy energy (CVN). Charpy tests at 0 °C were carried out. A marked increase in toughness of the base plate was found, as the date of fabrication increases. Diverse degrees of non-conformities, resulting in significant defects usually undetectable by external inspection, were found in the circumferential welds of 25% of all carafes manufactured before 1990. The number and criticality of these defects falls markedly in the carafes built after 1990. Serious errors during reconditioning, such as repairs of leaks and scratches, are indicative of a poor approach to the rehabilitation of the vessels. It is recommended to evaluate changes in the rehabilitation procedures and standards. A gradual process of substitution of the carafes built prior to 1990 is also recommended. © 2002 Elsevier Science Ltd. All rights reserved. |
publishDate |
2002 |
dc.date.none.fl_str_mv |
2002-11 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/54131 Fazzini, Pablo Gabriel; Santi, O.; Belmonte, Juan Carlos; Otegui, Luis Jose; Integrity and service life of LPG carafes; Elsevier; International Journal of Pressure Vessels and Piping; 79; 11; 11-2002; 767-775 0308-0161 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/54131 |
identifier_str_mv |
Fazzini, Pablo Gabriel; Santi, O.; Belmonte, Juan Carlos; Otegui, Luis Jose; Integrity and service life of LPG carafes; Elsevier; International Journal of Pressure Vessels and Piping; 79; 11; 11-2002; 767-775 0308-0161 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/doi/10.1016/S0308-0161(02)00010-8 info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0308016102000108 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier |
publisher.none.fl_str_mv |
Elsevier |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613355545821184 |
score |
13.070432 |