Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films
- Autores
- Haberkorn, Nestor Fabian; Bengió, Silvina; Suarez, Sergio Gabriel; Pérez, Pablo Daniel; Hofer, Juan Andres; Sirena, Martin
- Año de publicación
- 2019
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- We report on the influence of the disorder and stoichiometry in the resulting superconducting critical temperature of γ-Mo2N thin films. Initially, three films (with Tc values of 7.6 K, 6.8 K and 6 K) were grown at room temperature by reactive sputtering, on Si (1 0 0) using different N2/(Ar+N2) mixtures. The influence of the thermal annealing up to 973 K and irradiation damage produced by 1 MeV Zr+(fluence up 2 × 1014 cm−2) is analyzed. The Tc of pristine films remains unchanged for increasing irradiation doses up 2 × 1014 cm−2. The Tc for annealed films decreases close to the value expected for bulk samples (≈5 K) for increasing the annealing temperature. Successive irradiations of the annealed films tend to increase their Tc up to its initial values (before annealing). The results indicate that the Tc in nanometric grain size γ-Mo2N thin films is affected by both nitrogen stoichiometry and disorder at the atomic scale.
Fil: Haberkorn, Nestor Fabian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Bengió, Silvina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Suarez, Sergio Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina
Fil: Pérez, Pablo Daniel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Balseiro). División Colisiones Atómicas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina
Fil: Hofer, Juan Andres. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina
Fil: Sirena, Martin. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina - Materia
-
IRRADIATION
NITRIDES
SPUTTERING
SUPERCONDUCTIVITY - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/121255
Ver los metadatos del registro completo
id |
CONICETDig_b334255286c9b512ce42fcc8680e8186 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/121255 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin filmsEffect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline γ-Mo2N thin filmsHaberkorn, Nestor FabianBengió, SilvinaSuarez, Sergio GabrielPérez, Pablo DanielHofer, Juan AndresSirena, MartinIRRADIATIONNITRIDESSPUTTERINGSUPERCONDUCTIVITYhttps://purl.org/becyt/ford/1.3https://purl.org/becyt/ford/1We report on the influence of the disorder and stoichiometry in the resulting superconducting critical temperature of γ-Mo2N thin films. Initially, three films (with Tc values of 7.6 K, 6.8 K and 6 K) were grown at room temperature by reactive sputtering, on Si (1 0 0) using different N2/(Ar+N2) mixtures. The influence of the thermal annealing up to 973 K and irradiation damage produced by 1 MeV Zr+(fluence up 2 × 1014 cm−2) is analyzed. The Tc of pristine films remains unchanged for increasing irradiation doses up 2 × 1014 cm−2. The Tc for annealed films decreases close to the value expected for bulk samples (≈5 K) for increasing the annealing temperature. Successive irradiations of the annealed films tend to increase their Tc up to its initial values (before annealing). The results indicate that the Tc in nanometric grain size γ-Mo2N thin films is affected by both nitrogen stoichiometry and disorder at the atomic scale.Fil: Haberkorn, Nestor Fabian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaFil: Bengió, Silvina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaFil: Suarez, Sergio Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); ArgentinaFil: Pérez, Pablo Daniel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Balseiro). División Colisiones Atómicas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaFil: Hofer, Juan Andres. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); ArgentinaFil: Sirena, Martin. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; ArgentinaElsevier Science2019-02info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/121255Haberkorn, Nestor Fabian; Bengió, Silvina; Suarez, Sergio Gabriel; Pérez, Pablo Daniel; Hofer, Juan Andres; et al.; Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films; Elsevier Science; Materials Letters; 236; 2-2019; 252-2560167-577X1873-4979CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.matlet.2018.10.094info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S0167577X1831663Xinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:36:40Zoai:ri.conicet.gov.ar:11336/121255instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:36:41.081CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline γ-Mo2N thin films |
title |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films |
spellingShingle |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films Haberkorn, Nestor Fabian IRRADIATION NITRIDES SPUTTERING SUPERCONDUCTIVITY |
title_short |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films |
title_full |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films |
title_fullStr |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films |
title_full_unstemmed |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films |
title_sort |
Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films |
dc.creator.none.fl_str_mv |
Haberkorn, Nestor Fabian Bengió, Silvina Suarez, Sergio Gabriel Pérez, Pablo Daniel Hofer, Juan Andres Sirena, Martin |
author |
Haberkorn, Nestor Fabian |
author_facet |
Haberkorn, Nestor Fabian Bengió, Silvina Suarez, Sergio Gabriel Pérez, Pablo Daniel Hofer, Juan Andres Sirena, Martin |
author_role |
author |
author2 |
Bengió, Silvina Suarez, Sergio Gabriel Pérez, Pablo Daniel Hofer, Juan Andres Sirena, Martin |
author2_role |
author author author author author |
dc.subject.none.fl_str_mv |
IRRADIATION NITRIDES SPUTTERING SUPERCONDUCTIVITY |
topic |
IRRADIATION NITRIDES SPUTTERING SUPERCONDUCTIVITY |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/1.3 https://purl.org/becyt/ford/1 |
dc.description.none.fl_txt_mv |
We report on the influence of the disorder and stoichiometry in the resulting superconducting critical temperature of γ-Mo2N thin films. Initially, three films (with Tc values of 7.6 K, 6.8 K and 6 K) were grown at room temperature by reactive sputtering, on Si (1 0 0) using different N2/(Ar+N2) mixtures. The influence of the thermal annealing up to 973 K and irradiation damage produced by 1 MeV Zr+(fluence up 2 × 1014 cm−2) is analyzed. The Tc of pristine films remains unchanged for increasing irradiation doses up 2 × 1014 cm−2. The Tc for annealed films decreases close to the value expected for bulk samples (≈5 K) for increasing the annealing temperature. Successive irradiations of the annealed films tend to increase their Tc up to its initial values (before annealing). The results indicate that the Tc in nanometric grain size γ-Mo2N thin films is affected by both nitrogen stoichiometry and disorder at the atomic scale. Fil: Haberkorn, Nestor Fabian. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina Fil: Bengió, Silvina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina Fil: Suarez, Sergio Gabriel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina Fil: Pérez, Pablo Daniel. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Area Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Balseiro). División Colisiones Atómicas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina Fil: Hofer, Juan Andres. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina Fil: Sirena, Martin. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Patagonia Norte; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Investigación y Aplicaciones No Nucleares. Gerencia de Física (Centro Atómico Bariloche); Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Instituto Balseiro; Argentina |
description |
We report on the influence of the disorder and stoichiometry in the resulting superconducting critical temperature of γ-Mo2N thin films. Initially, three films (with Tc values of 7.6 K, 6.8 K and 6 K) were grown at room temperature by reactive sputtering, on Si (1 0 0) using different N2/(Ar+N2) mixtures. The influence of the thermal annealing up to 973 K and irradiation damage produced by 1 MeV Zr+(fluence up 2 × 1014 cm−2) is analyzed. The Tc of pristine films remains unchanged for increasing irradiation doses up 2 × 1014 cm−2. The Tc for annealed films decreases close to the value expected for bulk samples (≈5 K) for increasing the annealing temperature. Successive irradiations of the annealed films tend to increase their Tc up to its initial values (before annealing). The results indicate that the Tc in nanometric grain size γ-Mo2N thin films is affected by both nitrogen stoichiometry and disorder at the atomic scale. |
publishDate |
2019 |
dc.date.none.fl_str_mv |
2019-02 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/121255 Haberkorn, Nestor Fabian; Bengió, Silvina; Suarez, Sergio Gabriel; Pérez, Pablo Daniel; Hofer, Juan Andres; et al.; Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films; Elsevier Science; Materials Letters; 236; 2-2019; 252-256 0167-577X 1873-4979 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/121255 |
identifier_str_mv |
Haberkorn, Nestor Fabian; Bengió, Silvina; Suarez, Sergio Gabriel; Pérez, Pablo Daniel; Hofer, Juan Andres; et al.; Effect of thermal annealing and irradiation damage on the superconducting critical temperature of nanocrystalline gamma-Mo2N thin films; Elsevier Science; Materials Letters; 236; 2-2019; 252-256 0167-577X 1873-4979 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.matlet.2018.10.094 info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S0167577X1831663X |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier Science |
publisher.none.fl_str_mv |
Elsevier Science |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844613152714522624 |
score |
13.070432 |