Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases

Autores
Arencibia, Nicolas; Oestreicher, Víctor Santiago Jesús; Viva, Federico Andrés; Jobbagy, Matias
Año de publicación
2017
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
A family of monophasic nanoplatelets of Ni(ii)-Co(ii) layered hydroxides, were obtained by a one-pot room temperature homogeneous alkalinization driven by the the epoxide route with glycidol. Both cations precipitate in the form of solid solutions, giving the general formula Ni1-xCox(OH)2-yCly·nH2O. Co(ii)-rich samples developed the simonkolleite-like alpha structure in which cations can adopt either octahedral (Oh) or tetrahedral (Td) environments, according to the formula (Ni,Co)Oh1-xCoTd2x(OH)2-2x(Cl)2x·nH2O. Ni(ii)-rich ones resulted in ill-crystallized turbostratic (Ni,Co)1-x(OH)2-x(Cl)x·nH2O. Despite the inherent differences in the crystallochemical nature of theses phases, electrochemical measurements depict a monotonous behavior in terms of their capacitance. An optimum performance was observed for samples with XNi(II) = 0.83 under most of the experimental conditions explored. This sample reaches a maximum specific capacitance of 2091 F g-1, registered at a discharge current density of 0.5 A g-1, while an energy density of 80.7 W h kg-1 was recorded at a power density of 960.4 W kg-1.
Fil: Arencibia, Nicolas. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina
Fil: Oestreicher, Víctor Santiago Jesús. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina
Fil: Viva, Federico Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Constituyentes; Argentina
Fil: Jobbagy, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina
Materia
Ni(II)-Co(II)
Solid solutions
Supercapacitors
Electrochemistry
Synthesis
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/59221
Acceder
id CONICETDig_b17319512515ac955f2b9255ebee7f14
oai_identifier_str oai:ri.conicet.gov.ar:11336/59221
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phasesArencibia, NicolasOestreicher, Víctor Santiago JesúsViva, Federico AndrésJobbagy, MatiasNi(II)-Co(II)Solid solutionsSupercapacitorsElectrochemistrySynthesishttps://purl.org/becyt/ford/2.10https://purl.org/becyt/ford/2A family of monophasic nanoplatelets of Ni(ii)-Co(ii) layered hydroxides, were obtained by a one-pot room temperature homogeneous alkalinization driven by the the epoxide route with glycidol. Both cations precipitate in the form of solid solutions, giving the general formula Ni1-xCox(OH)2-yCly·nH2O. Co(ii)-rich samples developed the simonkolleite-like alpha structure in which cations can adopt either octahedral (Oh) or tetrahedral (Td) environments, according to the formula (Ni,Co)Oh1-xCoTd2x(OH)2-2x(Cl)2x·nH2O. Ni(ii)-rich ones resulted in ill-crystallized turbostratic (Ni,Co)1-x(OH)2-x(Cl)x·nH2O. Despite the inherent differences in the crystallochemical nature of theses phases, electrochemical measurements depict a monotonous behavior in terms of their capacitance. An optimum performance was observed for samples with XNi(II) = 0.83 under most of the experimental conditions explored. This sample reaches a maximum specific capacitance of 2091 F g-1, registered at a discharge current density of 0.5 A g-1, while an energy density of 80.7 W h kg-1 was recorded at a power density of 960.4 W kg-1.Fil: Arencibia, Nicolas. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; ArgentinaFil: Oestreicher, Víctor Santiago Jesús. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; ArgentinaFil: Viva, Federico Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Constituyentes; ArgentinaFil: Jobbagy, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; ArgentinaRoyal Society of Chemistry2017-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/59221Arencibia, Nicolas; Oestreicher, Víctor Santiago Jesús; Viva, Federico Andrés; Jobbagy, Matias; Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases; Royal Society of Chemistry; RSC Advances; 7; 10; 1-2017; 5595-56002046-2069CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1039/C6RA27839Finfo:eu-repo/semantics/altIdentifier/url/http://pubs.rsc.org/en/Content/ArticleLanding/2017/RA/C6RA27839Finfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-12-03T09:43:17Zoai:ri.conicet.gov.ar:11336/59221instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-12-03 09:43:17.94CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
title Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
spellingShingle Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
Arencibia, Nicolas
Ni(II)-Co(II)
Solid solutions
Supercapacitors
Electrochemistry
Synthesis
title_short Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
title_full Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
title_fullStr Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
title_full_unstemmed Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
title_sort Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases
dc.creator.none.fl_str_mv Arencibia, Nicolas
Oestreicher, Víctor Santiago Jesús
Viva, Federico Andrés
Jobbagy, Matias
author Arencibia, Nicolas
author_facet Arencibia, Nicolas
Oestreicher, Víctor Santiago Jesús
Viva, Federico Andrés
Jobbagy, Matias
author_role author
author2 Oestreicher, Víctor Santiago Jesús
Viva, Federico Andrés
Jobbagy, Matias
author2_role author
author
author
dc.subject.none.fl_str_mv Ni(II)-Co(II)
Solid solutions
Supercapacitors
Electrochemistry
Synthesis
topic Ni(II)-Co(II)
Solid solutions
Supercapacitors
Electrochemistry
Synthesis
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.10
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv A family of monophasic nanoplatelets of Ni(ii)-Co(ii) layered hydroxides, were obtained by a one-pot room temperature homogeneous alkalinization driven by the the epoxide route with glycidol. Both cations precipitate in the form of solid solutions, giving the general formula Ni1-xCox(OH)2-yCly·nH2O. Co(ii)-rich samples developed the simonkolleite-like alpha structure in which cations can adopt either octahedral (Oh) or tetrahedral (Td) environments, according to the formula (Ni,Co)Oh1-xCoTd2x(OH)2-2x(Cl)2x·nH2O. Ni(ii)-rich ones resulted in ill-crystallized turbostratic (Ni,Co)1-x(OH)2-x(Cl)x·nH2O. Despite the inherent differences in the crystallochemical nature of theses phases, electrochemical measurements depict a monotonous behavior in terms of their capacitance. An optimum performance was observed for samples with XNi(II) = 0.83 under most of the experimental conditions explored. This sample reaches a maximum specific capacitance of 2091 F g-1, registered at a discharge current density of 0.5 A g-1, while an energy density of 80.7 W h kg-1 was recorded at a power density of 960.4 W kg-1.
Fil: Arencibia, Nicolas. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina
Fil: Oestreicher, Víctor Santiago Jesús. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina
Fil: Viva, Federico Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comisión Nacional de Energía Atómica. Centro Atómico Constituyentes; Argentina
Fil: Jobbagy, Matias. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Ciudad Universitaria. Instituto de Química, Física de los Materiales, Medioambiente y Energía. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Instituto de Química, Física de los Materiales, Medioambiente y Energía; Argentina. Universidad de Buenos Aires. Facultad de Ciencias Exactas y Naturales. Departamento de Química Inorgánica, Analítica y Química Física; Argentina
description A family of monophasic nanoplatelets of Ni(ii)-Co(ii) layered hydroxides, were obtained by a one-pot room temperature homogeneous alkalinization driven by the the epoxide route with glycidol. Both cations precipitate in the form of solid solutions, giving the general formula Ni1-xCox(OH)2-yCly·nH2O. Co(ii)-rich samples developed the simonkolleite-like alpha structure in which cations can adopt either octahedral (Oh) or tetrahedral (Td) environments, according to the formula (Ni,Co)Oh1-xCoTd2x(OH)2-2x(Cl)2x·nH2O. Ni(ii)-rich ones resulted in ill-crystallized turbostratic (Ni,Co)1-x(OH)2-x(Cl)x·nH2O. Despite the inherent differences in the crystallochemical nature of theses phases, electrochemical measurements depict a monotonous behavior in terms of their capacitance. An optimum performance was observed for samples with XNi(II) = 0.83 under most of the experimental conditions explored. This sample reaches a maximum specific capacitance of 2091 F g-1, registered at a discharge current density of 0.5 A g-1, while an energy density of 80.7 W h kg-1 was recorded at a power density of 960.4 W kg-1.
publishDate 2017
dc.date.none.fl_str_mv 2017-01
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/59221
Arencibia, Nicolas; Oestreicher, Víctor Santiago Jesús; Viva, Federico Andrés; Jobbagy, Matias; Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases; Royal Society of Chemistry; RSC Advances; 7; 10; 1-2017; 5595-5600
2046-2069
CONICET Digital
CONICET
url http://hdl.handle.net/11336/59221
identifier_str_mv Arencibia, Nicolas; Oestreicher, Víctor Santiago Jesús; Viva, Federico Andrés; Jobbagy, Matias; Nanotextured alpha Ni(II)-Co(II) hydroxides as supercapacitive active phases; Royal Society of Chemistry; RSC Advances; 7; 10; 1-2017; 5595-5600
2046-2069
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1039/C6RA27839F
info:eu-repo/semantics/altIdentifier/url/http://pubs.rsc.org/en/Content/ArticleLanding/2017/RA/C6RA27839F
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Royal Society of Chemistry
publisher.none.fl_str_mv Royal Society of Chemistry
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1850505865513140224
score 13.227901

Publicaciones similares