Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment

Autores
Faccin, Federico; Prado, Andrea F.; Tomba Martinez, Analia Gladys; Ramajo, Leandro Alfredo
Año de publicación
2019
Idioma
español castellano
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In this work, the thermal shock response of commercial fireclay refractory castable with low alumina content was analyzed with the aim of evaluating the feasibility to be used as replacement of silicate-aluminate refractory bricks in a non-severe process. The study was performed in laboratory scale, with procedures especially designed based on the available standards, employing 2 commercial castables supplied by different manufacturers. Specimens cured for 24 h, 48 h and 7 days (for comparison with samples of civil concrete) were evaluated; some specimens were also thermally treated at 900 °C. As-received materials were characterized through granulometric analysis by sieving and X-ray diffraction. The specimens were mechanically tested in flexion and compression; moreover, the density, the porosity and the dynamic Young´s modulus of the samples were measured. The thermal shock test was performed by air cooling; after each cycle, the dynamic Young´s modulus was determined. At the end of the fifth cycle, the residual mechanical strength in flexion and compression was also determined. The results showed that the castable with finer granulometry and better mechanical performance before the thermal shock (castable A), was the most suitable to be used without a previous thermal treatment.
En este trabajo se analizó la respuesta al choque térmico de formulaciones comerciales de hormigones refractarios silicoaluminosos con el objetivo de evaluar la factibilidad de su uso como reemplazo de ladrillos refractarios de composición similar en aplicaciones de baja exigencia. El estudio se realizó a escala laboratorio, con procedimientos especialmente diseñados sobre la base de las normas disponibles, con 2 hormigones comerciales de diferentes proveedores. Se evaluaron probetas curadas por 24 h, 48 h y 7 días (para su correlato con probetas de hormigón civil). Algunas de las muestras fueron, además, tratadas térmicamente a 900 °C. Las formulaciones originales fueron caracterizadas mediante análisis granulométrico por tamizado y difracción de rayos X. Las probetas se probaron mecánicamente en flexión y compresión, y se determinaron la densidad, la porosidad, y el módulo elástico por excitación por impulso. El ensayo de choque térmico se llevó a cabo por enfriamiento en aire, luego de lo cual se determinó el módulo elástico dinámico. Al finalizar el quinto ciclo, se determinó la resistencia mecánica residual en flexión y compresión. Los resultados mostraron que el hormigón de granulometría más fina y de mejor desempeño mecánico antes del choque térmico (hormigón A) fue el material más adecuado para ser empleado sin pretratamiento térmico.
Fil: Faccin, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Prado, Andrea F.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Tomba Martinez, Analia Gladys. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Ramajo, Leandro Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Materia
Cementos de aluminatos cálcicos
Choque térmico
Hormigones refractarios
Refractory castables
Calcium aluminates cements
Thermal shock
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/120236
Acceder
id CONICETDig_9f81ba5e9b3bcce627d7581627afb06a
oai_identifier_str oai:ri.conicet.gov.ar:11336/120236
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatmentEvaluación de la resistencia al choque término de hormigones refractarios silicoaluminosos. Efecto del tratamiento térmicoFaccin, FedericoPrado, Andrea F.Tomba Martinez, Analia GladysRamajo, Leandro AlfredoCementos de aluminatos cálcicosChoque térmicoHormigones refractariosRefractory castablesCalcium aluminates cementsThermal shockhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2In this work, the thermal shock response of commercial fireclay refractory castable with low alumina content was analyzed with the aim of evaluating the feasibility to be used as replacement of silicate-aluminate refractory bricks in a non-severe process. The study was performed in laboratory scale, with procedures especially designed based on the available standards, employing 2 commercial castables supplied by different manufacturers. Specimens cured for 24 h, 48 h and 7 days (for comparison with samples of civil concrete) were evaluated; some specimens were also thermally treated at 900 °C. As-received materials were characterized through granulometric analysis by sieving and X-ray diffraction. The specimens were mechanically tested in flexion and compression; moreover, the density, the porosity and the dynamic Young´s modulus of the samples were measured. The thermal shock test was performed by air cooling; after each cycle, the dynamic Young´s modulus was determined. At the end of the fifth cycle, the residual mechanical strength in flexion and compression was also determined. The results showed that the castable with finer granulometry and better mechanical performance before the thermal shock (castable A), was the most suitable to be used without a previous thermal treatment.En este trabajo se analizó la respuesta al choque térmico de formulaciones comerciales de hormigones refractarios silicoaluminosos con el objetivo de evaluar la factibilidad de su uso como reemplazo de ladrillos refractarios de composición similar en aplicaciones de baja exigencia. El estudio se realizó a escala laboratorio, con procedimientos especialmente diseñados sobre la base de las normas disponibles, con 2 hormigones comerciales de diferentes proveedores. Se evaluaron probetas curadas por 24 h, 48 h y 7 días (para su correlato con probetas de hormigón civil). Algunas de las muestras fueron, además, tratadas térmicamente a 900 °C. Las formulaciones originales fueron caracterizadas mediante análisis granulométrico por tamizado y difracción de rayos X. Las probetas se probaron mecánicamente en flexión y compresión, y se determinaron la densidad, la porosidad, y el módulo elástico por excitación por impulso. El ensayo de choque térmico se llevó a cabo por enfriamiento en aire, luego de lo cual se determinó el módulo elástico dinámico. Al finalizar el quinto ciclo, se determinó la resistencia mecánica residual en flexión y compresión. Los resultados mostraron que el hormigón de granulometría más fina y de mejor desempeño mecánico antes del choque térmico (hormigón A) fue el material más adecuado para ser empleado sin pretratamiento térmico.Fil: Faccin, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Prado, Andrea F.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Tomba Martinez, Analia Gladys. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaFil: Ramajo, Leandro Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; ArgentinaSociedad Española de Cerámica y Vidrio2019-11info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/120236Faccin, Federico; Prado, Andrea F.; Tomba Martinez, Analia Gladys; Ramajo, Leandro Alfredo; Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment; Sociedad Española de Cerámica y Vidrio; Boletín de la Sociedad Española de Cerámica y Vidrio; 58; 6; 11-2019; 246-2542173-0431CONICET DigitalCONICETspainfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.bsecv.2019.05.002info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0366317519300445?via%3Dihubinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-10T13:07:28Zoai:ri.conicet.gov.ar:11336/120236instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-10 13:07:29.197CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
Evaluación de la resistencia al choque término de hormigones refractarios silicoaluminosos. Efecto del tratamiento térmico
title Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
spellingShingle Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
Faccin, Federico
Cementos de aluminatos cálcicos
Choque térmico
Hormigones refractarios
Refractory castables
Calcium aluminates cements
Thermal shock
title_short Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
title_full Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
title_fullStr Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
title_full_unstemmed Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
title_sort Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment
dc.creator.none.fl_str_mv Faccin, Federico
Prado, Andrea F.
Tomba Martinez, Analia Gladys
Ramajo, Leandro Alfredo
author Faccin, Federico
author_facet Faccin, Federico
Prado, Andrea F.
Tomba Martinez, Analia Gladys
Ramajo, Leandro Alfredo
author_role author
author2 Prado, Andrea F.
Tomba Martinez, Analia Gladys
Ramajo, Leandro Alfredo
author2_role author
author
author
dc.subject.none.fl_str_mv Cementos de aluminatos cálcicos
Choque térmico
Hormigones refractarios
Refractory castables
Calcium aluminates cements
Thermal shock
topic Cementos de aluminatos cálcicos
Choque térmico
Hormigones refractarios
Refractory castables
Calcium aluminates cements
Thermal shock
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv In this work, the thermal shock response of commercial fireclay refractory castable with low alumina content was analyzed with the aim of evaluating the feasibility to be used as replacement of silicate-aluminate refractory bricks in a non-severe process. The study was performed in laboratory scale, with procedures especially designed based on the available standards, employing 2 commercial castables supplied by different manufacturers. Specimens cured for 24 h, 48 h and 7 days (for comparison with samples of civil concrete) were evaluated; some specimens were also thermally treated at 900 °C. As-received materials were characterized through granulometric analysis by sieving and X-ray diffraction. The specimens were mechanically tested in flexion and compression; moreover, the density, the porosity and the dynamic Young´s modulus of the samples were measured. The thermal shock test was performed by air cooling; after each cycle, the dynamic Young´s modulus was determined. At the end of the fifth cycle, the residual mechanical strength in flexion and compression was also determined. The results showed that the castable with finer granulometry and better mechanical performance before the thermal shock (castable A), was the most suitable to be used without a previous thermal treatment.
En este trabajo se analizó la respuesta al choque térmico de formulaciones comerciales de hormigones refractarios silicoaluminosos con el objetivo de evaluar la factibilidad de su uso como reemplazo de ladrillos refractarios de composición similar en aplicaciones de baja exigencia. El estudio se realizó a escala laboratorio, con procedimientos especialmente diseñados sobre la base de las normas disponibles, con 2 hormigones comerciales de diferentes proveedores. Se evaluaron probetas curadas por 24 h, 48 h y 7 días (para su correlato con probetas de hormigón civil). Algunas de las muestras fueron, además, tratadas térmicamente a 900 °C. Las formulaciones originales fueron caracterizadas mediante análisis granulométrico por tamizado y difracción de rayos X. Las probetas se probaron mecánicamente en flexión y compresión, y se determinaron la densidad, la porosidad, y el módulo elástico por excitación por impulso. El ensayo de choque térmico se llevó a cabo por enfriamiento en aire, luego de lo cual se determinó el módulo elástico dinámico. Al finalizar el quinto ciclo, se determinó la resistencia mecánica residual en flexión y compresión. Los resultados mostraron que el hormigón de granulometría más fina y de mejor desempeño mecánico antes del choque térmico (hormigón A) fue el material más adecuado para ser empleado sin pretratamiento térmico.
Fil: Faccin, Federico. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Prado, Andrea F.. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Tomba Martinez, Analia Gladys. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
Fil: Ramajo, Leandro Alfredo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mar del Plata. Instituto de Investigaciones en Ciencia y Tecnología de Materiales. Universidad Nacional de Mar del Plata. Facultad de Ingeniería. Instituto de Investigaciones en Ciencia y Tecnología de Materiales; Argentina
description In this work, the thermal shock response of commercial fireclay refractory castable with low alumina content was analyzed with the aim of evaluating the feasibility to be used as replacement of silicate-aluminate refractory bricks in a non-severe process. The study was performed in laboratory scale, with procedures especially designed based on the available standards, employing 2 commercial castables supplied by different manufacturers. Specimens cured for 24 h, 48 h and 7 days (for comparison with samples of civil concrete) were evaluated; some specimens were also thermally treated at 900 °C. As-received materials were characterized through granulometric analysis by sieving and X-ray diffraction. The specimens were mechanically tested in flexion and compression; moreover, the density, the porosity and the dynamic Young´s modulus of the samples were measured. The thermal shock test was performed by air cooling; after each cycle, the dynamic Young´s modulus was determined. At the end of the fifth cycle, the residual mechanical strength in flexion and compression was also determined. The results showed that the castable with finer granulometry and better mechanical performance before the thermal shock (castable A), was the most suitable to be used without a previous thermal treatment.
publishDate 2019
dc.date.none.fl_str_mv 2019-11
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/120236
Faccin, Federico; Prado, Andrea F.; Tomba Martinez, Analia Gladys; Ramajo, Leandro Alfredo; Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment; Sociedad Española de Cerámica y Vidrio; Boletín de la Sociedad Española de Cerámica y Vidrio; 58; 6; 11-2019; 246-254
2173-0431
CONICET Digital
CONICET
url http://hdl.handle.net/11336/120236
identifier_str_mv Faccin, Federico; Prado, Andrea F.; Tomba Martinez, Analia Gladys; Ramajo, Leandro Alfredo; Evaluation of the thermal shock resistance of aluminate-silicate refractory castables. Effect of the thermal treatment; Sociedad Española de Cerámica y Vidrio; Boletín de la Sociedad Española de Cerámica y Vidrio; 58; 6; 11-2019; 246-254
2173-0431
CONICET Digital
CONICET
dc.language.none.fl_str_mv spa
language spa
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/j.bsecv.2019.05.002
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/pii/S0366317519300445?via%3Dihub
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Sociedad Española de Cerámica y Vidrio
publisher.none.fl_str_mv Sociedad Española de Cerámica y Vidrio
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842980335279669248
score 12.993085

Publicaciones similares