Optimization for Bone Samples Embedded in Methyl Methacrylate

Autores
Moreno Garcia, Maria Florencia; Martin, Alfredo Alberto; Fushimi, Shigeko; Feldman, Sara; Pastorino, Nina Fiorella; Juárez, Jorge Nicolás; Jammal, María Victoria; Missana, Liliana Raquel
Año de publicación
2022
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Our aim was to update a standard technique for embedding bone samples, with or without implants, using methyl methacrylate (MMA) to obtain reliable optical microscopy images from mineralized bone tissues and bone-implant interfaces. In addition, comparative studies were carried out using different temperatures throughout the polymerization process. Twenty-two New Zealand rabbit calvaria and femur bone samples with or without implants were used. The samples were fixed in 10% buffered formalin, dehydrated in an ascending alcohol series, and infiltrated in methyl methacrylate solutions (I, II and III). The specimens were divided into three groups. Groups 1 and 2 were polymerized at 24°C ± 5°C, while Group 3 was polymerized at 60°C. Group 1 and 2 obtained homogeneous, transparent, crystalline polymerization. Group 3 presented multiple bubbles (ø 2 – 3 mm), depressions, folds and even rupture of the vial container. The MMA bone samples polymerized at room temperature, showed good embedded, low hardness index, thin cuts, and effective staining.
Fil: Moreno Garcia, Maria Florencia. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina. Universidad Nacional de Tucuman. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Gobierno de la Provincia de Tucuman. Ministerio de Salud. Sistema Provincial de Salud. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnologico Conicet Noa Sur. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario.; Argentina
Fil: Martin, Alfredo Alberto. Universidad Nacional de Tucumán. Facultad de Agronomía y Zootecnia; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Fushimi, Shigeko. Okayama University; Japón
Fil: Feldman, Sara. Universidad Nacional de Rosario. Facultad de Cs.medicas. Laboratorio de Biologia Osteoarticular, Ingenieria Tisular y Terapias Emergentes; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Rosario; Argentina
Fil: Pastorino, Nina Fiorella. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina
Fil: Juárez, Jorge Nicolás. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina
Fil: Jammal, María Victoria. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina
Fil: Missana, Liliana Raquel. Universidad Nacional de Tucuman. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Gobierno de la Provincia de Tucuman. Ministerio de Salud. Sistema Provincial de Salud. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnologico Conicet Noa Sur. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario.; Argentina
Materia
BONE
FAST DECALCIFICATION
LARGE SAMPLES
METHYL METHACRYLATE
TEMPERATURE
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/224691
Acceder
id CONICETDig_9858c8f0fa4c1a5d5589490dd837fd47
oai_identifier_str oai:ri.conicet.gov.ar:11336/224691
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Optimization for Bone Samples Embedded in Methyl MethacrylateMoreno Garcia, Maria FlorenciaMartin, Alfredo AlbertoFushimi, ShigekoFeldman, SaraPastorino, Nina FiorellaJuárez, Jorge NicolásJammal, María VictoriaMissana, Liliana RaquelBONEFAST DECALCIFICATIONLARGE SAMPLESMETHYL METHACRYLATETEMPERATUREhttps://purl.org/becyt/ford/3.1https://purl.org/becyt/ford/3Our aim was to update a standard technique for embedding bone samples, with or without implants, using methyl methacrylate (MMA) to obtain reliable optical microscopy images from mineralized bone tissues and bone-implant interfaces. In addition, comparative studies were carried out using different temperatures throughout the polymerization process. Twenty-two New Zealand rabbit calvaria and femur bone samples with or without implants were used. The samples were fixed in 10% buffered formalin, dehydrated in an ascending alcohol series, and infiltrated in methyl methacrylate solutions (I, II and III). The specimens were divided into three groups. Groups 1 and 2 were polymerized at 24°C ± 5°C, while Group 3 was polymerized at 60°C. Group 1 and 2 obtained homogeneous, transparent, crystalline polymerization. Group 3 presented multiple bubbles (ø 2 – 3 mm), depressions, folds and even rupture of the vial container. The MMA bone samples polymerized at room temperature, showed good embedded, low hardness index, thin cuts, and effective staining.Fil: Moreno Garcia, Maria Florencia. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina. Universidad Nacional de Tucuman. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Gobierno de la Provincia de Tucuman. Ministerio de Salud. Sistema Provincial de Salud. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnologico Conicet Noa Sur. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario.; ArgentinaFil: Martin, Alfredo Alberto. Universidad Nacional de Tucumán. Facultad de Agronomía y Zootecnia; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; ArgentinaFil: Fushimi, Shigeko. Okayama University; JapónFil: Feldman, Sara. Universidad Nacional de Rosario. Facultad de Cs.medicas. Laboratorio de Biologia Osteoarticular, Ingenieria Tisular y Terapias Emergentes; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Rosario; ArgentinaFil: Pastorino, Nina Fiorella. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; ArgentinaFil: Juárez, Jorge Nicolás. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; ArgentinaFil: Jammal, María Victoria. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; ArgentinaFil: Missana, Liliana Raquel. Universidad Nacional de Tucuman. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Gobierno de la Provincia de Tucuman. Ministerio de Salud. Sistema Provincial de Salud. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnologico Conicet Noa Sur. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario.; ArgentinaThe Society for Hard Tissue Regenerative Biology2022-07info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/224691Moreno Garcia, Maria Florencia; Martin, Alfredo Alberto; Fushimi, Shigeko; Feldman, Sara; Pastorino, Nina Fiorella; et al.; Optimization for Bone Samples Embedded in Methyl Methacrylate; The Society for Hard Tissue Regenerative Biology; Journal of Hard Tissue Biology; 31; 3; 7-2022; 181-1861341-76491880-828XCONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://www.jstage.jst.go.jp/article/jhtb/31/3/31_181/_article/-char/ja/info:eu-repo/semantics/altIdentifier/doi/10.2485/jhtb.31.181info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-11-05T10:35:32Zoai:ri.conicet.gov.ar:11336/224691instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-11-05 10:35:32.57CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Optimization for Bone Samples Embedded in Methyl Methacrylate
title Optimization for Bone Samples Embedded in Methyl Methacrylate
spellingShingle Optimization for Bone Samples Embedded in Methyl Methacrylate
Moreno Garcia, Maria Florencia
BONE
FAST DECALCIFICATION
LARGE SAMPLES
METHYL METHACRYLATE
TEMPERATURE
title_short Optimization for Bone Samples Embedded in Methyl Methacrylate
title_full Optimization for Bone Samples Embedded in Methyl Methacrylate
title_fullStr Optimization for Bone Samples Embedded in Methyl Methacrylate
title_full_unstemmed Optimization for Bone Samples Embedded in Methyl Methacrylate
title_sort Optimization for Bone Samples Embedded in Methyl Methacrylate
dc.creator.none.fl_str_mv Moreno Garcia, Maria Florencia
Martin, Alfredo Alberto
Fushimi, Shigeko
Feldman, Sara
Pastorino, Nina Fiorella
Juárez, Jorge Nicolás
Jammal, María Victoria
Missana, Liliana Raquel
author Moreno Garcia, Maria Florencia
author_facet Moreno Garcia, Maria Florencia
Martin, Alfredo Alberto
Fushimi, Shigeko
Feldman, Sara
Pastorino, Nina Fiorella
Juárez, Jorge Nicolás
Jammal, María Victoria
Missana, Liliana Raquel
author_role author
author2 Martin, Alfredo Alberto
Fushimi, Shigeko
Feldman, Sara
Pastorino, Nina Fiorella
Juárez, Jorge Nicolás
Jammal, María Victoria
Missana, Liliana Raquel
author2_role author
author
author
author
author
author
author
dc.subject.none.fl_str_mv BONE
FAST DECALCIFICATION
LARGE SAMPLES
METHYL METHACRYLATE
TEMPERATURE
topic BONE
FAST DECALCIFICATION
LARGE SAMPLES
METHYL METHACRYLATE
TEMPERATURE
purl_subject.fl_str_mv https://purl.org/becyt/ford/3.1
https://purl.org/becyt/ford/3
dc.description.none.fl_txt_mv Our aim was to update a standard technique for embedding bone samples, with or without implants, using methyl methacrylate (MMA) to obtain reliable optical microscopy images from mineralized bone tissues and bone-implant interfaces. In addition, comparative studies were carried out using different temperatures throughout the polymerization process. Twenty-two New Zealand rabbit calvaria and femur bone samples with or without implants were used. The samples were fixed in 10% buffered formalin, dehydrated in an ascending alcohol series, and infiltrated in methyl methacrylate solutions (I, II and III). The specimens were divided into three groups. Groups 1 and 2 were polymerized at 24°C ± 5°C, while Group 3 was polymerized at 60°C. Group 1 and 2 obtained homogeneous, transparent, crystalline polymerization. Group 3 presented multiple bubbles (ø 2 – 3 mm), depressions, folds and even rupture of the vial container. The MMA bone samples polymerized at room temperature, showed good embedded, low hardness index, thin cuts, and effective staining.
Fil: Moreno Garcia, Maria Florencia. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina. Universidad Nacional de Tucuman. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Gobierno de la Provincia de Tucuman. Ministerio de Salud. Sistema Provincial de Salud. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnologico Conicet Noa Sur. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario.; Argentina
Fil: Martin, Alfredo Alberto. Universidad Nacional de Tucumán. Facultad de Agronomía y Zootecnia; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina
Fil: Fushimi, Shigeko. Okayama University; Japón
Fil: Feldman, Sara. Universidad Nacional de Rosario. Facultad de Cs.medicas. Laboratorio de Biologia Osteoarticular, Ingenieria Tisular y Terapias Emergentes; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Rosario; Argentina
Fil: Pastorino, Nina Fiorella. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina
Fil: Juárez, Jorge Nicolás. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina
Fil: Jammal, María Victoria. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de Tucumán. Facultad de Odontología. Cátedra de Anatomía Patológica. Laboratorio de Patología Molecular; Argentina
Fil: Missana, Liliana Raquel. Universidad Nacional de Tucuman. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Gobierno de la Provincia de Tucuman. Ministerio de Salud. Sistema Provincial de Salud. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario. - Consejo Nacional de Investigaciones Cientificas y Tecnicas. Centro Cientifico Tecnologico Conicet Noa Sur. Instituto de Investigaciones En Medicina Molecular y Celular Aplicada del Bicentenario.; Argentina
description Our aim was to update a standard technique for embedding bone samples, with or without implants, using methyl methacrylate (MMA) to obtain reliable optical microscopy images from mineralized bone tissues and bone-implant interfaces. In addition, comparative studies were carried out using different temperatures throughout the polymerization process. Twenty-two New Zealand rabbit calvaria and femur bone samples with or without implants were used. The samples were fixed in 10% buffered formalin, dehydrated in an ascending alcohol series, and infiltrated in methyl methacrylate solutions (I, II and III). The specimens were divided into three groups. Groups 1 and 2 were polymerized at 24°C ± 5°C, while Group 3 was polymerized at 60°C. Group 1 and 2 obtained homogeneous, transparent, crystalline polymerization. Group 3 presented multiple bubbles (ø 2 – 3 mm), depressions, folds and even rupture of the vial container. The MMA bone samples polymerized at room temperature, showed good embedded, low hardness index, thin cuts, and effective staining.
publishDate 2022
dc.date.none.fl_str_mv 2022-07
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/224691
Moreno Garcia, Maria Florencia; Martin, Alfredo Alberto; Fushimi, Shigeko; Feldman, Sara; Pastorino, Nina Fiorella; et al.; Optimization for Bone Samples Embedded in Methyl Methacrylate; The Society for Hard Tissue Regenerative Biology; Journal of Hard Tissue Biology; 31; 3; 7-2022; 181-186
1341-7649
1880-828X
CONICET Digital
CONICET
url http://hdl.handle.net/11336/224691
identifier_str_mv Moreno Garcia, Maria Florencia; Martin, Alfredo Alberto; Fushimi, Shigeko; Feldman, Sara; Pastorino, Nina Fiorella; et al.; Optimization for Bone Samples Embedded in Methyl Methacrylate; The Society for Hard Tissue Regenerative Biology; Journal of Hard Tissue Biology; 31; 3; 7-2022; 181-186
1341-7649
1880-828X
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://www.jstage.jst.go.jp/article/jhtb/31/3/31_181/_article/-char/ja/
info:eu-repo/semantics/altIdentifier/doi/10.2485/jhtb.31.181
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv The Society for Hard Tissue Regenerative Biology
publisher.none.fl_str_mv The Society for Hard Tissue Regenerative Biology
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1847978041973669888
score 13.121305

Publicaciones similares