Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application

Autores
Gomez Hoyos, Catalina; Vazquez, Analia
Año de publicación
2012
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Epoxy fique composites were evaluated for construction applications and compared with conventional wood used in construction. The composites studied were made with fique fibers treated using Na(OH) solution at 18 w/v%, untreated fique fibers were also used. The matrices were epoxy and epoxy with 5 wt.% of chemically modified C30B montmorillonite. Unidirectional composites of 90 mm × 20 mm × 4 mm were elaborated by pultrusion processing technique. The flexural properties loss occurred over 20 days of composites submitted to three types of environments: (i) water, (ii) saturated calcium hydroxide solution and (iii) mortar with w/c ratio of 0.45 and 540 kg/m3 of cement, cured in a saturated solution of lime stone at 50 °C. Results showed that fiber treatment and montmorillonite addition improved the flexural modulus and strength of composites in 40% and 34% respectively. Moreover the flexural properties of composites before and after ageing resulted comparable or even better than conventional wood used in construction.
Fil: Gomez Hoyos, Catalina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina; Argentina. Universidad de Buenos Aires. Facultad de Ingeniería; Argentina
Fil: Vazquez, Analia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina; Argentina. Universidad de Buenos Aires. Facultad de Ingeniería; Argentina
Materia
Polymermatrix Composites
Mechanical Properties
Mechanical Testing
Pultrusion
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/14761
Acceder
id CONICETDig_912b8622b85fa3d07d7b678ec0986323
oai_identifier_str oai:ri.conicet.gov.ar:11336/14761
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction applicationGomez Hoyos, CatalinaVazquez, AnaliaPolymermatrix CompositesMechanical PropertiesMechanical TestingPultrusionhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Epoxy fique composites were evaluated for construction applications and compared with conventional wood used in construction. The composites studied were made with fique fibers treated using Na(OH) solution at 18 w/v%, untreated fique fibers were also used. The matrices were epoxy and epoxy with 5 wt.% of chemically modified C30B montmorillonite. Unidirectional composites of 90 mm × 20 mm × 4 mm were elaborated by pultrusion processing technique. The flexural properties loss occurred over 20 days of composites submitted to three types of environments: (i) water, (ii) saturated calcium hydroxide solution and (iii) mortar with w/c ratio of 0.45 and 540 kg/m3 of cement, cured in a saturated solution of lime stone at 50 °C. Results showed that fiber treatment and montmorillonite addition improved the flexural modulus and strength of composites in 40% and 34% respectively. Moreover the flexural properties of composites before and after ageing resulted comparable or even better than conventional wood used in construction.Fil: Gomez Hoyos, Catalina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina; Argentina. Universidad de Buenos Aires. Facultad de Ingeniería; ArgentinaFil: Vazquez, Analia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina; Argentina. Universidad de Buenos Aires. Facultad de Ingeniería; ArgentinaElsevier2012-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/14761Gomez Hoyos, Catalina; Vazquez, Analia; Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application; Elsevier; Composites Part B: Engineering; 43; 8; 4-2012; 3120-31301359-8368enginfo:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S1359836812002661info:eu-repo/semantics/altIdentifier/doi/10.1016/j.compositesb.2012.04.027info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:08:52Zoai:ri.conicet.gov.ar:11336/14761instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:08:53.005CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
title Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
spellingShingle Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
Gomez Hoyos, Catalina
Polymermatrix Composites
Mechanical Properties
Mechanical Testing
Pultrusion
title_short Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
title_full Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
title_fullStr Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
title_full_unstemmed Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
title_sort Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application
dc.creator.none.fl_str_mv Gomez Hoyos, Catalina
Vazquez, Analia
author Gomez Hoyos, Catalina
author_facet Gomez Hoyos, Catalina
Vazquez, Analia
author_role author
author2 Vazquez, Analia
author2_role author
dc.subject.none.fl_str_mv Polymermatrix Composites
Mechanical Properties
Mechanical Testing
Pultrusion
topic Polymermatrix Composites
Mechanical Properties
Mechanical Testing
Pultrusion
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Epoxy fique composites were evaluated for construction applications and compared with conventional wood used in construction. The composites studied were made with fique fibers treated using Na(OH) solution at 18 w/v%, untreated fique fibers were also used. The matrices were epoxy and epoxy with 5 wt.% of chemically modified C30B montmorillonite. Unidirectional composites of 90 mm × 20 mm × 4 mm were elaborated by pultrusion processing technique. The flexural properties loss occurred over 20 days of composites submitted to three types of environments: (i) water, (ii) saturated calcium hydroxide solution and (iii) mortar with w/c ratio of 0.45 and 540 kg/m3 of cement, cured in a saturated solution of lime stone at 50 °C. Results showed that fiber treatment and montmorillonite addition improved the flexural modulus and strength of composites in 40% and 34% respectively. Moreover the flexural properties of composites before and after ageing resulted comparable or even better than conventional wood used in construction.
Fil: Gomez Hoyos, Catalina. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina; Argentina. Universidad de Buenos Aires. Facultad de Ingeniería; Argentina
Fil: Vazquez, Analia. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina; Argentina. Universidad de Buenos Aires. Facultad de Ingeniería; Argentina
description Epoxy fique composites were evaluated for construction applications and compared with conventional wood used in construction. The composites studied were made with fique fibers treated using Na(OH) solution at 18 w/v%, untreated fique fibers were also used. The matrices were epoxy and epoxy with 5 wt.% of chemically modified C30B montmorillonite. Unidirectional composites of 90 mm × 20 mm × 4 mm were elaborated by pultrusion processing technique. The flexural properties loss occurred over 20 days of composites submitted to three types of environments: (i) water, (ii) saturated calcium hydroxide solution and (iii) mortar with w/c ratio of 0.45 and 540 kg/m3 of cement, cured in a saturated solution of lime stone at 50 °C. Results showed that fiber treatment and montmorillonite addition improved the flexural modulus and strength of composites in 40% and 34% respectively. Moreover the flexural properties of composites before and after ageing resulted comparable or even better than conventional wood used in construction.
publishDate 2012
dc.date.none.fl_str_mv 2012-04
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/14761
Gomez Hoyos, Catalina; Vazquez, Analia; Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application; Elsevier; Composites Part B: Engineering; 43; 8; 4-2012; 3120-3130
1359-8368
url http://hdl.handle.net/11336/14761
identifier_str_mv Gomez Hoyos, Catalina; Vazquez, Analia; Flexural properties loss of unidirectional epoxy/fique composites immersed in water and alkaline medium for construction application; Elsevier; Composites Part B: Engineering; 43; 8; 4-2012; 3120-3130
1359-8368
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S1359836812002661
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.compositesb.2012.04.027
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844613961190735872
score 13.070432

Publicaciones similares