Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties

Autores
Chanquia, Corina Mercedes; Cánepa, Analía Laura; Bazán Aguirre, Juliá; Sapag, Manuel Karim; Rodríguez-Castellón, Enrique; Reyes, Patricio David; Herrero, Eduardo Renato; Casuscelli, Sandra Graciela; Eimer, Griselda Alejandra
Año de publicación
2012
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
M41S type mesoporous silicate particles with spherical morphology containing copper nano-species were successfully synthesized by the template-ion exchange (TIE) method and compared with those synthesized by the direct hydrothermal (DHT) method. Various techniques including XRD, AAS, adsorption/ desorption of N2, SEM, TEM, TGA, UV–Vis-DRS, TPR, XPS and FT-IR-Py, were employed for the nanocatalysts characterization. A narrow distribution of silicate particle size between 2 and 3 lm, and a primary mesoporosity were evidenced by electronic microscopy, even for loadings of copper of about 7 wt.%. All the materials exhibited a good structural regularity, besides of high surface areas (>1000 m2/g) and pore volumes ( 1 cm3/g). A secondary mesoporosity, likely caused by the hydrothermal treatment during the TIE process, was also detected. This new synthesis method showed the advantage of promoting the introduction of copper nano-species to the mesostructure (isolated Cud+ species and [Cud+. . .Od . . .Cud+]n clusters), minimizing the bulk CuO formation. The coexistence of both oxidation states 1+ and 2+ (d+) in the major copper species present in these catalysts could be inferred. In addition, all of the samples only showed Lewis acid sites. The cyclohexene oxidation with H2O2 has been studied as a catalytic test: the highly dispersed Cud+ species on the mesopore walls, obtained by TIE method, have been suggested as the main active sites for the oxidation. The allylic oxidation has mainly taken place, with the formation of 2-cyclohexen-1-one and 2-cyclohexen-1-ol as major products.
Fil: Chanquia, Corina Mercedes. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Consejo Nacional de Investigaciones Cientificas y Tecnicas. Oficina de Coordinacion Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia - Nodo Bariloche | Comision Nacional de Energia Atomica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia - Nodo Bariloche.; Argentina
Fil: Cánepa, Analía Laura. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Bazán Aguirre, Juliá. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Sapag, Manuel Karim. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Universidad Nacional de San Luis; Argentina
Fil: Rodríguez-Castellón, Enrique. Universidad de Málaga; España
Fil: Reyes, Patricio David. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mendoza. Instituto Argentino de Investigaciones de las Zonas Áridas. Provincia de Mendoza. Instituto Argentino de Investigaciones de las Zonas Áridas. Universidad Nacional de Cuyo. Instituto Argentino de Investigaciones de las Zonas Áridas; Argentina
Fil: Herrero, Eduardo Renato. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Casuscelli, Sandra Graciela. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Eimer, Griselda Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Materia
COPPER
NANO-SPECIES
TEMPLATE-ION EXCHANGE
M41S
OXIDATION TEST
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/110639
Acceder
id CONICETDig_8d1317ec3ffe2ee898ca026bd21a1ef9
oai_identifier_str oai:ri.conicet.gov.ar:11336/110639
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation propertiesChanquia, Corina MercedesCánepa, Analía LauraBazán Aguirre, JuliáSapag, Manuel KarimRodríguez-Castellón, EnriqueReyes, Patricio DavidHerrero, Eduardo RenatoCasuscelli, Sandra GracielaEimer, Griselda AlejandraCOPPERNANO-SPECIESTEMPLATE-ION EXCHANGEM41SOXIDATION TESThttps://purl.org/becyt/ford/2.4https://purl.org/becyt/ford/2M41S type mesoporous silicate particles with spherical morphology containing copper nano-species were successfully synthesized by the template-ion exchange (TIE) method and compared with those synthesized by the direct hydrothermal (DHT) method. Various techniques including XRD, AAS, adsorption/ desorption of N2, SEM, TEM, TGA, UV–Vis-DRS, TPR, XPS and FT-IR-Py, were employed for the nanocatalysts characterization. A narrow distribution of silicate particle size between 2 and 3 lm, and a primary mesoporosity were evidenced by electronic microscopy, even for loadings of copper of about 7 wt.%. All the materials exhibited a good structural regularity, besides of high surface areas (>1000 m2/g) and pore volumes ( 1 cm3/g). A secondary mesoporosity, likely caused by the hydrothermal treatment during the TIE process, was also detected. This new synthesis method showed the advantage of promoting the introduction of copper nano-species to the mesostructure (isolated Cud+ species and [Cud+. . .Od . . .Cud+]n clusters), minimizing the bulk CuO formation. The coexistence of both oxidation states 1+ and 2+ (d+) in the major copper species present in these catalysts could be inferred. In addition, all of the samples only showed Lewis acid sites. The cyclohexene oxidation with H2O2 has been studied as a catalytic test: the highly dispersed Cud+ species on the mesopore walls, obtained by TIE method, have been suggested as the main active sites for the oxidation. The allylic oxidation has mainly taken place, with the formation of 2-cyclohexen-1-one and 2-cyclohexen-1-ol as major products.Fil: Chanquia, Corina Mercedes. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Consejo Nacional de Investigaciones Cientificas y Tecnicas. Oficina de Coordinacion Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia - Nodo Bariloche | Comision Nacional de Energia Atomica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia - Nodo Bariloche.; ArgentinaFil: Cánepa, Analía Laura. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; ArgentinaFil: Bazán Aguirre, Juliá. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; ArgentinaFil: Sapag, Manuel Karim. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Universidad Nacional de San Luis; ArgentinaFil: Rodríguez-Castellón, Enrique. Universidad de Málaga; EspañaFil: Reyes, Patricio David. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mendoza. Instituto Argentino de Investigaciones de las Zonas Áridas. Provincia de Mendoza. Instituto Argentino de Investigaciones de las Zonas Áridas. Universidad Nacional de Cuyo. Instituto Argentino de Investigaciones de las Zonas Áridas; ArgentinaFil: Herrero, Eduardo Renato. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; ArgentinaFil: Casuscelli, Sandra Graciela. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; ArgentinaFil: Eimer, Griselda Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; ArgentinaElsevier Science2012-03info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/110639Chanquia, Corina Mercedes; Cánepa, Analía Laura; Bazán Aguirre, Juliá; Sapag, Manuel Karim; Rodríguez-Castellón, Enrique; et al.; Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties; Elsevier Science; Microporous and Mesoporous Materials; 151; 3-2012; 2-121387-1811CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/doi/10.1016/j.micromeso.2011.07.001info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S1387181111003167info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T10:01:08Zoai:ri.conicet.gov.ar:11336/110639instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 10:01:08.705CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
title Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
spellingShingle Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
Chanquia, Corina Mercedes
COPPER
NANO-SPECIES
TEMPLATE-ION EXCHANGE
M41S
OXIDATION TEST
title_short Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
title_full Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
title_fullStr Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
title_full_unstemmed Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
title_sort Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties
dc.creator.none.fl_str_mv Chanquia, Corina Mercedes
Cánepa, Analía Laura
Bazán Aguirre, Juliá
Sapag, Manuel Karim
Rodríguez-Castellón, Enrique
Reyes, Patricio David
Herrero, Eduardo Renato
Casuscelli, Sandra Graciela
Eimer, Griselda Alejandra
author Chanquia, Corina Mercedes
author_facet Chanquia, Corina Mercedes
Cánepa, Analía Laura
Bazán Aguirre, Juliá
Sapag, Manuel Karim
Rodríguez-Castellón, Enrique
Reyes, Patricio David
Herrero, Eduardo Renato
Casuscelli, Sandra Graciela
Eimer, Griselda Alejandra
author_role author
author2 Cánepa, Analía Laura
Bazán Aguirre, Juliá
Sapag, Manuel Karim
Rodríguez-Castellón, Enrique
Reyes, Patricio David
Herrero, Eduardo Renato
Casuscelli, Sandra Graciela
Eimer, Griselda Alejandra
author2_role author
author
author
author
author
author
author
author
dc.subject.none.fl_str_mv COPPER
NANO-SPECIES
TEMPLATE-ION EXCHANGE
M41S
OXIDATION TEST
topic COPPER
NANO-SPECIES
TEMPLATE-ION EXCHANGE
M41S
OXIDATION TEST
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.4
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv M41S type mesoporous silicate particles with spherical morphology containing copper nano-species were successfully synthesized by the template-ion exchange (TIE) method and compared with those synthesized by the direct hydrothermal (DHT) method. Various techniques including XRD, AAS, adsorption/ desorption of N2, SEM, TEM, TGA, UV–Vis-DRS, TPR, XPS and FT-IR-Py, were employed for the nanocatalysts characterization. A narrow distribution of silicate particle size between 2 and 3 lm, and a primary mesoporosity were evidenced by electronic microscopy, even for loadings of copper of about 7 wt.%. All the materials exhibited a good structural regularity, besides of high surface areas (>1000 m2/g) and pore volumes ( 1 cm3/g). A secondary mesoporosity, likely caused by the hydrothermal treatment during the TIE process, was also detected. This new synthesis method showed the advantage of promoting the introduction of copper nano-species to the mesostructure (isolated Cud+ species and [Cud+. . .Od . . .Cud+]n clusters), minimizing the bulk CuO formation. The coexistence of both oxidation states 1+ and 2+ (d+) in the major copper species present in these catalysts could be inferred. In addition, all of the samples only showed Lewis acid sites. The cyclohexene oxidation with H2O2 has been studied as a catalytic test: the highly dispersed Cud+ species on the mesopore walls, obtained by TIE method, have been suggested as the main active sites for the oxidation. The allylic oxidation has mainly taken place, with the formation of 2-cyclohexen-1-one and 2-cyclohexen-1-ol as major products.
Fil: Chanquia, Corina Mercedes. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Consejo Nacional de Investigaciones Cientificas y Tecnicas. Oficina de Coordinacion Administrativa Ciudad Universitaria. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia - Nodo Bariloche | Comision Nacional de Energia Atomica. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia. Unidad Ejecutora Instituto de Nanociencia y Nanotecnologia - Nodo Bariloche.; Argentina
Fil: Cánepa, Analía Laura. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Bazán Aguirre, Juliá. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Sapag, Manuel Karim. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Universidad Nacional de San Luis; Argentina
Fil: Rodríguez-Castellón, Enrique. Universidad de Málaga; España
Fil: Reyes, Patricio David. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Mendoza. Instituto Argentino de Investigaciones de las Zonas Áridas. Provincia de Mendoza. Instituto Argentino de Investigaciones de las Zonas Áridas. Universidad Nacional de Cuyo. Instituto Argentino de Investigaciones de las Zonas Áridas; Argentina
Fil: Herrero, Eduardo Renato. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Casuscelli, Sandra Graciela. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
Fil: Eimer, Griselda Alejandra. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigación y Tecnología Química. Universidad Tecnológica Nacional. Facultad Regional Córdoba. Centro de Investigación y Tecnología Química; Argentina
description M41S type mesoporous silicate particles with spherical morphology containing copper nano-species were successfully synthesized by the template-ion exchange (TIE) method and compared with those synthesized by the direct hydrothermal (DHT) method. Various techniques including XRD, AAS, adsorption/ desorption of N2, SEM, TEM, TGA, UV–Vis-DRS, TPR, XPS and FT-IR-Py, were employed for the nanocatalysts characterization. A narrow distribution of silicate particle size between 2 and 3 lm, and a primary mesoporosity were evidenced by electronic microscopy, even for loadings of copper of about 7 wt.%. All the materials exhibited a good structural regularity, besides of high surface areas (>1000 m2/g) and pore volumes ( 1 cm3/g). A secondary mesoporosity, likely caused by the hydrothermal treatment during the TIE process, was also detected. This new synthesis method showed the advantage of promoting the introduction of copper nano-species to the mesostructure (isolated Cud+ species and [Cud+. . .Od . . .Cud+]n clusters), minimizing the bulk CuO formation. The coexistence of both oxidation states 1+ and 2+ (d+) in the major copper species present in these catalysts could be inferred. In addition, all of the samples only showed Lewis acid sites. The cyclohexene oxidation with H2O2 has been studied as a catalytic test: the highly dispersed Cud+ species on the mesopore walls, obtained by TIE method, have been suggested as the main active sites for the oxidation. The allylic oxidation has mainly taken place, with the formation of 2-cyclohexen-1-one and 2-cyclohexen-1-ol as major products.
publishDate 2012
dc.date.none.fl_str_mv 2012-03
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/110639
Chanquia, Corina Mercedes; Cánepa, Analía Laura; Bazán Aguirre, Juliá; Sapag, Manuel Karim; Rodríguez-Castellón, Enrique; et al.; Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties; Elsevier Science; Microporous and Mesoporous Materials; 151; 3-2012; 2-12
1387-1811
CONICET Digital
CONICET
url http://hdl.handle.net/11336/110639
identifier_str_mv Chanquia, Corina Mercedes; Cánepa, Analía Laura; Bazán Aguirre, Juliá; Sapag, Manuel Karim; Rodríguez-Castellón, Enrique; et al.; Copper-containing spherical mesoporous silicates prepared by template-ion exchange: A multitechnique characterization and oxidation properties; Elsevier Science; Microporous and Mesoporous Materials; 151; 3-2012; 2-12
1387-1811
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/doi/10.1016/j.micromeso.2011.07.001
info:eu-repo/semantics/altIdentifier/url/https://www.sciencedirect.com/science/article/abs/pii/S1387181111003167
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier Science
publisher.none.fl_str_mv Elsevier Science
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269678162935808
score 12.885934

Publicaciones similares