Mullite macro-needles for reinforcement of refractory castables
- Autores
- Mocciaro, Anabella; Cimas, Axel Javier; Rendtorff Birrer, Nicolás Maximiliano; Scian, Alberto Nestor
- Año de publicación
- 2022
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- Ceramic macro-needles incorporation as reinforcement in commercial refractory castable was studied. Ceramic macro-needles (Ø2x20 mm) were made from kaolinite clay and gibbsite to obtain mullite as the main crystalline phase. Specimens with the ceramic reinforcement were evaluated by compression after being treated at two temperatures (815 and 1400 °C). The results were compared with those obtained using the same commercial concrete but reinforced with steel fibers and without reinforcement. Compression values presented by specimens with ceramic macro-needles were 74% and 50% higher than specimens with steel fibers after exposition to 815 and 1400 °C, respectively. Based on these results, it was established that ceramic macro-needles are a feasible solution to improve the mechanical resistance of castables exposed to high temperatures.
Fil: Mocciaro, Anabella. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Cimas, Axel Javier. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina
Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina
Fil: Scian, Alberto Nestor. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina - Materia
-
FIBERS
MECHANICAL PROPERTIES
REFRACTORIES - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by-nc/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/213008
Ver los metadatos del registro completo
id |
CONICETDig_78c53ad2e3b347a8ed1a88c9e0dfb6ab |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/213008 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Mullite macro-needles for reinforcement of refractory castablesMocciaro, AnabellaCimas, Axel JavierRendtorff Birrer, Nicolás MaximilianoScian, Alberto NestorFIBERSMECHANICAL PROPERTIESREFRACTORIEShttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Ceramic macro-needles incorporation as reinforcement in commercial refractory castable was studied. Ceramic macro-needles (Ø2x20 mm) were made from kaolinite clay and gibbsite to obtain mullite as the main crystalline phase. Specimens with the ceramic reinforcement were evaluated by compression after being treated at two temperatures (815 and 1400 °C). The results were compared with those obtained using the same commercial concrete but reinforced with steel fibers and without reinforcement. Compression values presented by specimens with ceramic macro-needles were 74% and 50% higher than specimens with steel fibers after exposition to 815 and 1400 °C, respectively. Based on these results, it was established that ceramic macro-needles are a feasible solution to improve the mechanical resistance of castables exposed to high temperatures.Fil: Mocciaro, Anabella. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Cimas, Axel Javier. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaFil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; ArgentinaFil: Scian, Alberto Nestor. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; ArgentinaAssociação Brasileira de Cerâmica2022-12info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/213008Mocciaro, Anabella; Cimas, Axel Javier; Rendtorff Birrer, Nicolás Maximiliano; Scian, Alberto Nestor; Mullite macro-needles for reinforcement of refractory castables; Associação Brasileira de Cerâmica; Ceramica; 68; 388; 12-2022; 420-4260366-69131678-4553CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132022000400420&tlng=eninfo:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132022683883342info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T09:52:52Zoai:ri.conicet.gov.ar:11336/213008instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 09:52:52.775CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Mullite macro-needles for reinforcement of refractory castables |
title |
Mullite macro-needles for reinforcement of refractory castables |
spellingShingle |
Mullite macro-needles for reinforcement of refractory castables Mocciaro, Anabella FIBERS MECHANICAL PROPERTIES REFRACTORIES |
title_short |
Mullite macro-needles for reinforcement of refractory castables |
title_full |
Mullite macro-needles for reinforcement of refractory castables |
title_fullStr |
Mullite macro-needles for reinforcement of refractory castables |
title_full_unstemmed |
Mullite macro-needles for reinforcement of refractory castables |
title_sort |
Mullite macro-needles for reinforcement of refractory castables |
dc.creator.none.fl_str_mv |
Mocciaro, Anabella Cimas, Axel Javier Rendtorff Birrer, Nicolás Maximiliano Scian, Alberto Nestor |
author |
Mocciaro, Anabella |
author_facet |
Mocciaro, Anabella Cimas, Axel Javier Rendtorff Birrer, Nicolás Maximiliano Scian, Alberto Nestor |
author_role |
author |
author2 |
Cimas, Axel Javier Rendtorff Birrer, Nicolás Maximiliano Scian, Alberto Nestor |
author2_role |
author author author |
dc.subject.none.fl_str_mv |
FIBERS MECHANICAL PROPERTIES REFRACTORIES |
topic |
FIBERS MECHANICAL PROPERTIES REFRACTORIES |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.5 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
Ceramic macro-needles incorporation as reinforcement in commercial refractory castable was studied. Ceramic macro-needles (Ø2x20 mm) were made from kaolinite clay and gibbsite to obtain mullite as the main crystalline phase. Specimens with the ceramic reinforcement were evaluated by compression after being treated at two temperatures (815 and 1400 °C). The results were compared with those obtained using the same commercial concrete but reinforced with steel fibers and without reinforcement. Compression values presented by specimens with ceramic macro-needles were 74% and 50% higher than specimens with steel fibers after exposition to 815 and 1400 °C, respectively. Based on these results, it was established that ceramic macro-needles are a feasible solution to improve the mechanical resistance of castables exposed to high temperatures. Fil: Mocciaro, Anabella. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Cimas, Axel Javier. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina Fil: Rendtorff Birrer, Nicolás Maximiliano. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina Fil: Scian, Alberto Nestor. Universidad Nacional de La Plata. Facultad de Ciencias Exactas. Departamento de Química; Argentina. Provincia de Buenos Aires. Gobernación. Comisión de Investigaciones Científicas. Centro de Tecnología de Recursos Minerales y Cerámica. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Tecnología de Recursos Minerales y Cerámica; Argentina |
description |
Ceramic macro-needles incorporation as reinforcement in commercial refractory castable was studied. Ceramic macro-needles (Ø2x20 mm) were made from kaolinite clay and gibbsite to obtain mullite as the main crystalline phase. Specimens with the ceramic reinforcement were evaluated by compression after being treated at two temperatures (815 and 1400 °C). The results were compared with those obtained using the same commercial concrete but reinforced with steel fibers and without reinforcement. Compression values presented by specimens with ceramic macro-needles were 74% and 50% higher than specimens with steel fibers after exposition to 815 and 1400 °C, respectively. Based on these results, it was established that ceramic macro-needles are a feasible solution to improve the mechanical resistance of castables exposed to high temperatures. |
publishDate |
2022 |
dc.date.none.fl_str_mv |
2022-12 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/213008 Mocciaro, Anabella; Cimas, Axel Javier; Rendtorff Birrer, Nicolás Maximiliano; Scian, Alberto Nestor; Mullite macro-needles for reinforcement of refractory castables; Associação Brasileira de Cerâmica; Ceramica; 68; 388; 12-2022; 420-426 0366-6913 1678-4553 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/213008 |
identifier_str_mv |
Mocciaro, Anabella; Cimas, Axel Javier; Rendtorff Birrer, Nicolás Maximiliano; Scian, Alberto Nestor; Mullite macro-needles for reinforcement of refractory castables; Associação Brasileira de Cerâmica; Ceramica; 68; 388; 12-2022; 420-426 0366-6913 1678-4553 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://www.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132022000400420&tlng=en info:eu-repo/semantics/altIdentifier/doi/10.1590/0366-69132022683883342 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by-nc/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by-nc/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Associação Brasileira de Cerâmica |
publisher.none.fl_str_mv |
Associação Brasileira de Cerâmica |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1842269188117233664 |
score |
13.13397 |