Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions

Autores
Kramer, Gustavo Raul; Méndez, Marcela Claudia; Ares, Alicia Esther
Año de publicación
2018
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In the present research, we studied the corrosion resistance of commercial aluminum alloys exposed to ethanol produced in the northeastern region of Argentina and to commercial ethanol as reference medium. Electrochemical tests of potentiodynamic polarization and weight loss were performed by immersion at temperatures below the boiling point of ethanol (25 °C, 40 °C and 50 °C). The results showed that the increase in the corrosion rate of the alloys is directly proportional to the increase in the temperature of the solution, and that the combined action of contaminants in the alcohol (water, organic acids or aggressive ions) contributed to the increase in the aggressiveness of the environment. Specifically, through the results of the gravimetric tests, corrosion products characteristic of the formation of pitting corrosion and alkoxidation were observed. In contrast to the above, the existence of the pitting corrosion mechanism was demonstrated by defining a pitting potential in the potentiodynamic polarization curves.
Fil: Kramer, Gustavo Raul. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; Argentina
Fil: Méndez, Marcela Claudia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; Argentina
Fil: Ares, Alicia Esther. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; Argentina
Materia
ALUMINUM ALLOYS
CORROSION
ETHANOL
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/87298
Acceder
id CONICETDig_5f0db7f422816bed2bf35e57f222ecf7
oai_identifier_str oai:ri.conicet.gov.ar:11336/87298
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutionsKramer, Gustavo RaulMéndez, Marcela ClaudiaAres, Alicia EstherALUMINUM ALLOYSCORROSIONETHANOLhttps://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2In the present research, we studied the corrosion resistance of commercial aluminum alloys exposed to ethanol produced in the northeastern region of Argentina and to commercial ethanol as reference medium. Electrochemical tests of potentiodynamic polarization and weight loss were performed by immersion at temperatures below the boiling point of ethanol (25 °C, 40 °C and 50 °C). The results showed that the increase in the corrosion rate of the alloys is directly proportional to the increase in the temperature of the solution, and that the combined action of contaminants in the alcohol (water, organic acids or aggressive ions) contributed to the increase in the aggressiveness of the environment. Specifically, through the results of the gravimetric tests, corrosion products characteristic of the formation of pitting corrosion and alkoxidation were observed. In contrast to the above, the existence of the pitting corrosion mechanism was demonstrated by defining a pitting potential in the potentiodynamic polarization curves.Fil: Kramer, Gustavo Raul. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; ArgentinaFil: Méndez, Marcela Claudia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; ArgentinaFil: Ares, Alicia Esther. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; ArgentinaUniversidade Federal de São Carlos2018-10info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/87298Kramer, Gustavo Raul; Méndez, Marcela Claudia; Ares, Alicia Esther; Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions; Universidade Federal de São Carlos; Materials Research; 21; 6; 10-2018; 1-121980-53731516-1439CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://ref.scielo.org/k3xjqhinfo:eu-repo/semantics/altIdentifier/doi/10.1590/1980-5373-mr-2017-0272info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-03T10:04:12Zoai:ri.conicet.gov.ar:11336/87298instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-03 10:04:13.229CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
title Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
spellingShingle Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
Kramer, Gustavo Raul
ALUMINUM ALLOYS
CORROSION
ETHANOL
title_short Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
title_full Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
title_fullStr Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
title_full_unstemmed Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
title_sort Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions
dc.creator.none.fl_str_mv Kramer, Gustavo Raul
Méndez, Marcela Claudia
Ares, Alicia Esther
author Kramer, Gustavo Raul
author_facet Kramer, Gustavo Raul
Méndez, Marcela Claudia
Ares, Alicia Esther
author_role author
author2 Méndez, Marcela Claudia
Ares, Alicia Esther
author2_role author
author
dc.subject.none.fl_str_mv ALUMINUM ALLOYS
CORROSION
ETHANOL
topic ALUMINUM ALLOYS
CORROSION
ETHANOL
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv In the present research, we studied the corrosion resistance of commercial aluminum alloys exposed to ethanol produced in the northeastern region of Argentina and to commercial ethanol as reference medium. Electrochemical tests of potentiodynamic polarization and weight loss were performed by immersion at temperatures below the boiling point of ethanol (25 °C, 40 °C and 50 °C). The results showed that the increase in the corrosion rate of the alloys is directly proportional to the increase in the temperature of the solution, and that the combined action of contaminants in the alcohol (water, organic acids or aggressive ions) contributed to the increase in the aggressiveness of the environment. Specifically, through the results of the gravimetric tests, corrosion products characteristic of the formation of pitting corrosion and alkoxidation were observed. In contrast to the above, the existence of the pitting corrosion mechanism was demonstrated by defining a pitting potential in the potentiodynamic polarization curves.
Fil: Kramer, Gustavo Raul. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; Argentina
Fil: Méndez, Marcela Claudia. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; Argentina
Fil: Ares, Alicia Esther. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Nordeste. Instituto de Materiales de Misiones. Universidad Nacional de Misiones. Facultad de Ciencias Exactas Químicas y Naturales. Instituto de Materiales de Misiones; Argentina
description In the present research, we studied the corrosion resistance of commercial aluminum alloys exposed to ethanol produced in the northeastern region of Argentina and to commercial ethanol as reference medium. Electrochemical tests of potentiodynamic polarization and weight loss were performed by immersion at temperatures below the boiling point of ethanol (25 °C, 40 °C and 50 °C). The results showed that the increase in the corrosion rate of the alloys is directly proportional to the increase in the temperature of the solution, and that the combined action of contaminants in the alcohol (water, organic acids or aggressive ions) contributed to the increase in the aggressiveness of the environment. Specifically, through the results of the gravimetric tests, corrosion products characteristic of the formation of pitting corrosion and alkoxidation were observed. In contrast to the above, the existence of the pitting corrosion mechanism was demonstrated by defining a pitting potential in the potentiodynamic polarization curves.
publishDate 2018
dc.date.none.fl_str_mv 2018-10
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/87298
Kramer, Gustavo Raul; Méndez, Marcela Claudia; Ares, Alicia Esther; Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions; Universidade Federal de São Carlos; Materials Research; 21; 6; 10-2018; 1-12
1980-5373
1516-1439
CONICET Digital
CONICET
url http://hdl.handle.net/11336/87298
identifier_str_mv Kramer, Gustavo Raul; Méndez, Marcela Claudia; Ares, Alicia Esther; Evaluation of corrosion resistance of commercial aluminum alloys in ethanol solutions; Universidade Federal de São Carlos; Materials Research; 21; 6; 10-2018; 1-12
1980-5373
1516-1439
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://ref.scielo.org/k3xjqh
info:eu-repo/semantics/altIdentifier/doi/10.1590/1980-5373-mr-2017-0272
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Universidade Federal de São Carlos
publisher.none.fl_str_mv Universidade Federal de São Carlos
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1842269844164050944
score 13.13397

Publicaciones similares