Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties

Autores
Miranda, Carlos Darío; Villarroel Rocha, Dimar; Sapag, Manuel Karim; Lopez, Carlos Alberto; Pedregosa, Jose Carmelo; Alonso, José Antonio
Año de publicación
2021
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Crystal structure and properties of Sr11Mo4O23treated at 1100 and 1400 °C were studiedviasynchrotron X-ray powder diffraction and thermogravimetric analysis, coupled with mass spectrometry. Synchrotron studies reveal the crystallographic effect of the annealing temperature, showing that the lowest-temperature phase must be defined in a triclinic symmetry, in contrast to the cubic one obtained at 1400 °C. The mass spectrometry allowed the identification of the released compounds during the thermogravimetric analysis, thus unveiling the physicochemical behavior of the sample during the heating process. Furthermore, an aging analysis was made, confirming the superior stability of this sample when it is treated at 1400 °C. Finally, an optimized sintering procedure allowed us to obtain a superior density and hence the highest conductivity measured so far for this system.
Fil: Miranda, Carlos Darío. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Villarroel Rocha, Dimar. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina
Fil: Sapag, Manuel Karim. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina
Fil: Lopez, Carlos Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Pedregosa, Jose Carmelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Alonso, José Antonio. Consejo Superior de Investigaciones Científicas; España
Materia
Sr11Mo4O23
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/171858
Acceder
id CONICETDig_44e405bcd40fad4bbc2535d16bf22a3a
oai_identifier_str oai:ri.conicet.gov.ar:11336/171858
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport propertiesMiranda, Carlos DaríoVillarroel Rocha, DimarSapag, Manuel KarimLopez, Carlos AlbertoPedregosa, Jose CarmeloAlonso, José AntonioSr11Mo4O23https://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1Crystal structure and properties of Sr11Mo4O23treated at 1100 and 1400 °C were studiedviasynchrotron X-ray powder diffraction and thermogravimetric analysis, coupled with mass spectrometry. Synchrotron studies reveal the crystallographic effect of the annealing temperature, showing that the lowest-temperature phase must be defined in a triclinic symmetry, in contrast to the cubic one obtained at 1400 °C. The mass spectrometry allowed the identification of the released compounds during the thermogravimetric analysis, thus unveiling the physicochemical behavior of the sample during the heating process. Furthermore, an aging analysis was made, confirming the superior stability of this sample when it is treated at 1400 °C. Finally, an optimized sintering procedure allowed us to obtain a superior density and hence the highest conductivity measured so far for this system.Fil: Miranda, Carlos Darío. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Villarroel Rocha, Dimar. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; ArgentinaFil: Sapag, Manuel Karim. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; ArgentinaFil: Lopez, Carlos Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Pedregosa, Jose Carmelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; ArgentinaFil: Alonso, José Antonio. Consejo Superior de Investigaciones Científicas; EspañaRoyal Society of Chemistry2021-04info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/171858Miranda, Carlos Darío; Villarroel Rocha, Dimar; Sapag, Manuel Karim; Lopez, Carlos Alberto; Pedregosa, Jose Carmelo; et al.; Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties; Royal Society of Chemistry; RSC Advances; 11; 23; 4-2021; 13814-138202046-2069CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/https://pubs.rsc.org/en/content/articlelanding/2021/ra/d0ra10620hinfo:eu-repo/semantics/altIdentifier/doi/10.1039/d0ra10620hinfo:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:32:35Zoai:ri.conicet.gov.ar:11336/171858instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:32:35.586CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
title Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
spellingShingle Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
Miranda, Carlos Darío
Sr11Mo4O23
title_short Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
title_full Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
title_fullStr Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
title_full_unstemmed Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
title_sort Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties
dc.creator.none.fl_str_mv Miranda, Carlos Darío
Villarroel Rocha, Dimar
Sapag, Manuel Karim
Lopez, Carlos Alberto
Pedregosa, Jose Carmelo
Alonso, José Antonio
author Miranda, Carlos Darío
author_facet Miranda, Carlos Darío
Villarroel Rocha, Dimar
Sapag, Manuel Karim
Lopez, Carlos Alberto
Pedregosa, Jose Carmelo
Alonso, José Antonio
author_role author
author2 Villarroel Rocha, Dimar
Sapag, Manuel Karim
Lopez, Carlos Alberto
Pedregosa, Jose Carmelo
Alonso, José Antonio
author2_role author
author
author
author
author
dc.subject.none.fl_str_mv Sr11Mo4O23
topic Sr11Mo4O23
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.4
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv Crystal structure and properties of Sr11Mo4O23treated at 1100 and 1400 °C were studiedviasynchrotron X-ray powder diffraction and thermogravimetric analysis, coupled with mass spectrometry. Synchrotron studies reveal the crystallographic effect of the annealing temperature, showing that the lowest-temperature phase must be defined in a triclinic symmetry, in contrast to the cubic one obtained at 1400 °C. The mass spectrometry allowed the identification of the released compounds during the thermogravimetric analysis, thus unveiling the physicochemical behavior of the sample during the heating process. Furthermore, an aging analysis was made, confirming the superior stability of this sample when it is treated at 1400 °C. Finally, an optimized sintering procedure allowed us to obtain a superior density and hence the highest conductivity measured so far for this system.
Fil: Miranda, Carlos Darío. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Villarroel Rocha, Dimar. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina
Fil: Sapag, Manuel Karim. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich". Universidad Nacional de San Luis. Facultad de Ciencias Físico Matemáticas y Naturales. Instituto de Física Aplicada "Dr. Jorge Andrés Zgrablich"; Argentina
Fil: Lopez, Carlos Alberto. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Pedregosa, Jose Carmelo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - San Luis. Instituto de Investigaciones en Tecnología Química. Universidad Nacional de San Luis. Facultad de Química, Bioquímica y Farmacia. Instituto de Investigaciones en Tecnología Química; Argentina
Fil: Alonso, José Antonio. Consejo Superior de Investigaciones Científicas; España
description Crystal structure and properties of Sr11Mo4O23treated at 1100 and 1400 °C were studiedviasynchrotron X-ray powder diffraction and thermogravimetric analysis, coupled with mass spectrometry. Synchrotron studies reveal the crystallographic effect of the annealing temperature, showing that the lowest-temperature phase must be defined in a triclinic symmetry, in contrast to the cubic one obtained at 1400 °C. The mass spectrometry allowed the identification of the released compounds during the thermogravimetric analysis, thus unveiling the physicochemical behavior of the sample during the heating process. Furthermore, an aging analysis was made, confirming the superior stability of this sample when it is treated at 1400 °C. Finally, an optimized sintering procedure allowed us to obtain a superior density and hence the highest conductivity measured so far for this system.
publishDate 2021
dc.date.none.fl_str_mv 2021-04
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/171858
Miranda, Carlos Darío; Villarroel Rocha, Dimar; Sapag, Manuel Karim; Lopez, Carlos Alberto; Pedregosa, Jose Carmelo; et al.; Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties; Royal Society of Chemistry; RSC Advances; 11; 23; 4-2021; 13814-13820
2046-2069
CONICET Digital
CONICET
url http://hdl.handle.net/11336/171858
identifier_str_mv Miranda, Carlos Darío; Villarroel Rocha, Dimar; Sapag, Manuel Karim; Lopez, Carlos Alberto; Pedregosa, Jose Carmelo; et al.; Synthesis conditions impact on Sr11Mo4O23electroceramic: crystal structure, stability and transport properties; Royal Society of Chemistry; RSC Advances; 11; 23; 4-2021; 13814-13820
2046-2069
CONICET Digital
CONICET
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/https://pubs.rsc.org/en/content/articlelanding/2021/ra/d0ra10620h
info:eu-repo/semantics/altIdentifier/doi/10.1039/d0ra10620h
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Royal Society of Chemistry
publisher.none.fl_str_mv Royal Society of Chemistry
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844614339705700352
score 13.070432

Publicaciones similares