Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years
- Autores
- Santillan, Lautaro Rodolfo; Locati, Francisco; Villagrán Zaccardi, Yury Andrés; Zega, Claudio Javier
- Año de publicación
- 2020
- Idioma
- inglés
- Tipo de recurso
- artículo
- Estado
- versión publicada
- Descripción
- The effect of recycled concrete aggregate (RCA) on concrete performance against external sulfate attack (ESA) is not yet fully known. In this paper, recycled aggregate concretes (RAC) with 0, 50, 75 and 100% of RCA contents were evaluated after 10 years of exposure immersed in 50g/l sodium sulfate solution. Sulfate ingress profiles were obtained by wet chemical analyses and FRX. Also, the mineralogy of the ingress profile was evaluated by thermogravimetric analyses. Finally, microcracking development in samples was evaluated by optical fluorescent microscopy image analysis. Although RAC showed a slight increase in sulfate ingress, due to its higher porosity (about 30% higher SO3 content near the surface for 50% or higher replacement ratio than control concrete), a dense new matrix still allows a good performance of RAC to external sulfate attack with even 100% RCA content.
El efecto del árido reciclado de hormigón (AR) en el desempeño del hormigón frente al ataque externo por sulfatos (AES) no es aún del todo conocido. En este trabajo, se evaluaron hormigones con áridos reciclados (HAR) con 0, 50, 75 y 100% de AR, tras 10 años sumergidos en solución de sulfato de sodio 50g/l. Se obtuvieron perfiles de ingreso de sulfato mediante análisis químico vía húmeda y FRX. También se evaluó la mineralogía de los perfiles por termogravimetría y la microfisuración mediante microscopia óptica con fluorescencia. Aunque los HAR mostraron un leve incremento en el ingreso de sulfatos debido a su mayor porosidad (aproximadamente 30% más de SO3 en la superficie para reemplazos de 50% o mayores), una nueva matriz densa permite un aceptable desempeño del HAR frente al AES, aún con un 100% de AR.
Fil: Santillan, Lautaro Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; Argentina
Fil: Locati, Francisco. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigaciones en Ciencias de la Tierra. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas Físicas y Naturales. Centro de Investigaciones en Ciencias de la Tierra; Argentina
Fil: Villagrán Zaccardi, Yury Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; Argentina
Fil: Zega, Claudio Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; Argentina - Materia
-
CONCRETE
TRANSPORT PROPERTIES
SULPHATE ATTACK
MICROCRACKING
THERMAL ANALYSIS - Nivel de accesibilidad
- acceso abierto
- Condiciones de uso
- https://creativecommons.org/licenses/by/2.5/ar/
- Repositorio
- Institución
- Consejo Nacional de Investigaciones Científicas y Técnicas
- OAI Identificador
- oai:ri.conicet.gov.ar:11336/133334
Ver los metadatos del registro completo
id |
CONICETDig_36d62856a02bdb3102591c58d4ace307 |
---|---|
oai_identifier_str |
oai:ri.conicet.gov.ar:11336/133334 |
network_acronym_str |
CONICETDig |
repository_id_str |
3498 |
network_name_str |
CONICET Digital (CONICET) |
spelling |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 yearsAtaque por sulfatos a largo plazo sobre hormigón de árido reciclado sumergido en solución de sulfato de sodio por 10 añosSantillan, Lautaro RodolfoLocati, FranciscoVillagrán Zaccardi, Yury AndrésZega, Claudio JavierCONCRETETRANSPORT PROPERTIESSULPHATE ATTACKMICROCRACKINGTHERMAL ANALYSIShttps://purl.org/becyt/ford/2.1https://purl.org/becyt/ford/2The effect of recycled concrete aggregate (RCA) on concrete performance against external sulfate attack (ESA) is not yet fully known. In this paper, recycled aggregate concretes (RAC) with 0, 50, 75 and 100% of RCA contents were evaluated after 10 years of exposure immersed in 50g/l sodium sulfate solution. Sulfate ingress profiles were obtained by wet chemical analyses and FRX. Also, the mineralogy of the ingress profile was evaluated by thermogravimetric analyses. Finally, microcracking development in samples was evaluated by optical fluorescent microscopy image analysis. Although RAC showed a slight increase in sulfate ingress, due to its higher porosity (about 30% higher SO3 content near the surface for 50% or higher replacement ratio than control concrete), a dense new matrix still allows a good performance of RAC to external sulfate attack with even 100% RCA content.El efecto del árido reciclado de hormigón (AR) en el desempeño del hormigón frente al ataque externo por sulfatos (AES) no es aún del todo conocido. En este trabajo, se evaluaron hormigones con áridos reciclados (HAR) con 0, 50, 75 y 100% de AR, tras 10 años sumergidos en solución de sulfato de sodio 50g/l. Se obtuvieron perfiles de ingreso de sulfato mediante análisis químico vía húmeda y FRX. También se evaluó la mineralogía de los perfiles por termogravimetría y la microfisuración mediante microscopia óptica con fluorescencia. Aunque los HAR mostraron un leve incremento en el ingreso de sulfatos debido a su mayor porosidad (aproximadamente 30% más de SO3 en la superficie para reemplazos de 50% o mayores), una nueva matriz densa permite un aceptable desempeño del HAR frente al AES, aún con un 100% de AR.Fil: Santillan, Lautaro Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; ArgentinaFil: Locati, Francisco. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigaciones en Ciencias de la Tierra. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas Físicas y Naturales. Centro de Investigaciones en Ciencias de la Tierra; ArgentinaFil: Villagrán Zaccardi, Yury Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; ArgentinaFil: Zega, Claudio Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; ArgentinaInstituto de Ciencias de la Construcción Eduardo Torroja2020-02info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/133334Santillan, Lautaro Rodolfo; Locati, Francisco; Villagrán Zaccardi, Yury Andrés; Zega, Claudio Javier; Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years; Instituto de Ciencias de la Construcción Eduardo Torroja; Materiales de Construccion; 70; 337; 2-2020; 1-140465-27461988-3226CONICET DigitalCONICETenginfo:eu-repo/semantics/altIdentifier/url/http://materconstrucc.revistas.csic.es/index.php/materconstrucc/article/view/2279info:eu-repo/semantics/altIdentifier/doi/10.3989/mc.2020.06319info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T10:26:51Zoai:ri.conicet.gov.ar:11336/133334instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 10:26:51.798CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse |
dc.title.none.fl_str_mv |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years Ataque por sulfatos a largo plazo sobre hormigón de árido reciclado sumergido en solución de sulfato de sodio por 10 años |
title |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years |
spellingShingle |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years Santillan, Lautaro Rodolfo CONCRETE TRANSPORT PROPERTIES SULPHATE ATTACK MICROCRACKING THERMAL ANALYSIS |
title_short |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years |
title_full |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years |
title_fullStr |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years |
title_full_unstemmed |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years |
title_sort |
Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years |
dc.creator.none.fl_str_mv |
Santillan, Lautaro Rodolfo Locati, Francisco Villagrán Zaccardi, Yury Andrés Zega, Claudio Javier |
author |
Santillan, Lautaro Rodolfo |
author_facet |
Santillan, Lautaro Rodolfo Locati, Francisco Villagrán Zaccardi, Yury Andrés Zega, Claudio Javier |
author_role |
author |
author2 |
Locati, Francisco Villagrán Zaccardi, Yury Andrés Zega, Claudio Javier |
author2_role |
author author author |
dc.subject.none.fl_str_mv |
CONCRETE TRANSPORT PROPERTIES SULPHATE ATTACK MICROCRACKING THERMAL ANALYSIS |
topic |
CONCRETE TRANSPORT PROPERTIES SULPHATE ATTACK MICROCRACKING THERMAL ANALYSIS |
purl_subject.fl_str_mv |
https://purl.org/becyt/ford/2.1 https://purl.org/becyt/ford/2 |
dc.description.none.fl_txt_mv |
The effect of recycled concrete aggregate (RCA) on concrete performance against external sulfate attack (ESA) is not yet fully known. In this paper, recycled aggregate concretes (RAC) with 0, 50, 75 and 100% of RCA contents were evaluated after 10 years of exposure immersed in 50g/l sodium sulfate solution. Sulfate ingress profiles were obtained by wet chemical analyses and FRX. Also, the mineralogy of the ingress profile was evaluated by thermogravimetric analyses. Finally, microcracking development in samples was evaluated by optical fluorescent microscopy image analysis. Although RAC showed a slight increase in sulfate ingress, due to its higher porosity (about 30% higher SO3 content near the surface for 50% or higher replacement ratio than control concrete), a dense new matrix still allows a good performance of RAC to external sulfate attack with even 100% RCA content. El efecto del árido reciclado de hormigón (AR) en el desempeño del hormigón frente al ataque externo por sulfatos (AES) no es aún del todo conocido. En este trabajo, se evaluaron hormigones con áridos reciclados (HAR) con 0, 50, 75 y 100% de AR, tras 10 años sumergidos en solución de sulfato de sodio 50g/l. Se obtuvieron perfiles de ingreso de sulfato mediante análisis químico vía húmeda y FRX. También se evaluó la mineralogía de los perfiles por termogravimetría y la microfisuración mediante microscopia óptica con fluorescencia. Aunque los HAR mostraron un leve incremento en el ingreso de sulfatos debido a su mayor porosidad (aproximadamente 30% más de SO3 en la superficie para reemplazos de 50% o mayores), una nueva matriz densa permite un aceptable desempeño del HAR frente al AES, aún con un 100% de AR. Fil: Santillan, Lautaro Rodolfo. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; Argentina Fil: Locati, Francisco. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - Córdoba. Centro de Investigaciones en Ciencias de la Tierra. Universidad Nacional de Córdoba. Facultad de Ciencias Exactas Físicas y Naturales. Centro de Investigaciones en Ciencias de la Tierra; Argentina Fil: Villagrán Zaccardi, Yury Andrés. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; Argentina Fil: Zega, Claudio Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata; Argentina. Laboratorio de Entrenamiento Multidisciplinario para la Investigación Tecnológica; Argentina |
description |
The effect of recycled concrete aggregate (RCA) on concrete performance against external sulfate attack (ESA) is not yet fully known. In this paper, recycled aggregate concretes (RAC) with 0, 50, 75 and 100% of RCA contents were evaluated after 10 years of exposure immersed in 50g/l sodium sulfate solution. Sulfate ingress profiles were obtained by wet chemical analyses and FRX. Also, the mineralogy of the ingress profile was evaluated by thermogravimetric analyses. Finally, microcracking development in samples was evaluated by optical fluorescent microscopy image analysis. Although RAC showed a slight increase in sulfate ingress, due to its higher porosity (about 30% higher SO3 content near the surface for 50% or higher replacement ratio than control concrete), a dense new matrix still allows a good performance of RAC to external sulfate attack with even 100% RCA content. |
publishDate |
2020 |
dc.date.none.fl_str_mv |
2020-02 |
dc.type.none.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion http://purl.org/coar/resource_type/c_6501 info:ar-repo/semantics/articulo |
format |
article |
status_str |
publishedVersion |
dc.identifier.none.fl_str_mv |
http://hdl.handle.net/11336/133334 Santillan, Lautaro Rodolfo; Locati, Francisco; Villagrán Zaccardi, Yury Andrés; Zega, Claudio Javier; Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years; Instituto de Ciencias de la Construcción Eduardo Torroja; Materiales de Construccion; 70; 337; 2-2020; 1-14 0465-2746 1988-3226 CONICET Digital CONICET |
url |
http://hdl.handle.net/11336/133334 |
identifier_str_mv |
Santillan, Lautaro Rodolfo; Locati, Francisco; Villagrán Zaccardi, Yury Andrés; Zega, Claudio Javier; Long-term sulfate attack on recycled aggregate concrete immersed in sodium sulfate solution for 10 years; Instituto de Ciencias de la Construcción Eduardo Torroja; Materiales de Construccion; 70; 337; 2-2020; 1-14 0465-2746 1988-3226 CONICET Digital CONICET |
dc.language.none.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
info:eu-repo/semantics/altIdentifier/url/http://materconstrucc.revistas.csic.es/index.php/materconstrucc/article/view/2279 info:eu-repo/semantics/altIdentifier/doi/10.3989/mc.2020.06319 |
dc.rights.none.fl_str_mv |
info:eu-repo/semantics/openAccess https://creativecommons.org/licenses/by/2.5/ar/ |
eu_rights_str_mv |
openAccess |
rights_invalid_str_mv |
https://creativecommons.org/licenses/by/2.5/ar/ |
dc.format.none.fl_str_mv |
application/pdf application/pdf application/pdf |
dc.publisher.none.fl_str_mv |
Instituto de Ciencias de la Construcción Eduardo Torroja |
publisher.none.fl_str_mv |
Instituto de Ciencias de la Construcción Eduardo Torroja |
dc.source.none.fl_str_mv |
reponame:CONICET Digital (CONICET) instname:Consejo Nacional de Investigaciones Científicas y Técnicas |
reponame_str |
CONICET Digital (CONICET) |
collection |
CONICET Digital (CONICET) |
instname_str |
Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.name.fl_str_mv |
CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas |
repository.mail.fl_str_mv |
dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar |
_version_ |
1844614270168334336 |
score |
13.070432 |