One-step room temperature synthesis of very small g-Fe2O3 nanoparticles

Autores
Moscoso Londoño, Oscar; Carrião Dos Santos, Marcus; Cosio Castañeda, C.; Bilovol, Vitaliy; Martinez Sanchez, R.; Lede, Eduardo Javier; Socolovsky, Leandro Martin; Martinez Garcia, Ricardo
Año de publicación
2013
Idioma
inglés
Tipo de recurso
artículo
Estado
versión publicada
Descripción
Very small maghemite nanoparticles (~3 nm) are obtained through a one-step synthesis at room temperature. The fast neutralization reaction of a ferric solution in a basic medium produces an intermediate phase, presumably two-line ferrihydrite, which in oxidizing conditions is transformed to maghemite nanoparticles. The synthesis of maghemite, as final product of the reaction, was characterized by High-Resolution Transmission Electron Microscopy (HR-TEM), X-ray Absorption Fine Structure (XAFS), Mössbauer spectroscopy, and magnetometry. The XAFS technique allowed the analysis of the crystallographic variations into maghemite nanoparticles as a result of modification in its surface/volume ratio. Mössbauer spectroscopy at low temperature (4.2 K) confirms the presence of Fe(III) in tetrahedral and octahedral interstices, in the stoichiometry corresponding to maghemite. The specific magnetization, M vs H (3 K and 300 K, up to 7 T) and temperature dependence of the magnetization (50 Oe by ZFC mode, 2 K < T < 300 K) indicate that maghemite nanoparticles of 3 nm are in superparamagnetic state with a blocking temperature close to 36 K.
Fil: Moscoso Londoño, Oscar. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Carrião Dos Santos, Marcus. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina. Universidade Federal de Goias; Brasil
Fil: Cosio Castañeda, C.. Universidad Nacional Autónoma de México; México. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Bilovol, Vitaliy. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Martinez Sanchez, R.. Universidad de la Habana; Cuba
Fil: Lede, Eduardo Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Socolovsky, Leandro Martin. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Martinez Garcia, Ricardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Materia
Oxides
Chemical Synthesis
Mossbauer Spectroscopy
Xafs (Exafs And Xanes)
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/6565
Acceder
id CONICETDig_1bd78ebbdb10032dc27178538c003e6e
oai_identifier_str oai:ri.conicet.gov.ar:11336/6565
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling One-step room temperature synthesis of very small g-Fe2O3 nanoparticlesMoscoso Londoño, OscarCarrião Dos Santos, MarcusCosio Castañeda, C.Bilovol, VitaliyMartinez Sanchez, R.Lede, Eduardo JavierSocolovsky, Leandro MartinMartinez Garcia, RicardoOxidesChemical SynthesisMossbauer SpectroscopyXafs (Exafs And Xanes)https://purl.org/becyt/ford/2.5https://purl.org/becyt/ford/2Very small maghemite nanoparticles (~3 nm) are obtained through a one-step synthesis at room temperature. The fast neutralization reaction of a ferric solution in a basic medium produces an intermediate phase, presumably two-line ferrihydrite, which in oxidizing conditions is transformed to maghemite nanoparticles. The synthesis of maghemite, as final product of the reaction, was characterized by High-Resolution Transmission Electron Microscopy (HR-TEM), X-ray Absorption Fine Structure (XAFS), Mössbauer spectroscopy, and magnetometry. The XAFS technique allowed the analysis of the crystallographic variations into maghemite nanoparticles as a result of modification in its surface/volume ratio. Mössbauer spectroscopy at low temperature (4.2 K) confirms the presence of Fe(III) in tetrahedral and octahedral interstices, in the stoichiometry corresponding to maghemite. The specific magnetization, M vs H (3 K and 300 K, up to 7 T) and temperature dependence of the magnetization (50 Oe by ZFC mode, 2 K < T < 300 K) indicate that maghemite nanoparticles of 3 nm are in superparamagnetic state with a blocking temperature close to 36 K.Fil: Moscoso Londoño, Oscar. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; ArgentinaFil: Carrião Dos Santos, Marcus. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina. Universidade Federal de Goias; BrasilFil: Cosio Castañeda, C.. Universidad Nacional Autónoma de México; México. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; ArgentinaFil: Bilovol, Vitaliy. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; ArgentinaFil: Martinez Sanchez, R.. Universidad de la Habana; CubaFil: Lede, Eduardo Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; ArgentinaFil: Socolovsky, Leandro Martin. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; ArgentinaFil: Martinez Garcia, Ricardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; ArgentinaElsevier2013-05info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/6565Moscoso Londoño, Oscar; Carrião Dos Santos, Marcus; Cosio Castañeda, C.; Bilovol, Vitaliy; Martinez Sanchez, R.; et al.; One-step room temperature synthesis of very small g-Fe2O3 nanoparticles; Elsevier; Materials Research Bulletin; 48; 5-2013; 3474-34780025-5408enginfo:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0025540813004078info:eu-repo/semantics/altIdentifier/doi/10.1016/j.materresbull.2013.05.042info:eu-repo/semantics/altIdentifier/doi/info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-nd/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-10-22T11:25:02Zoai:ri.conicet.gov.ar:11336/6565instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-10-22 11:25:03.279CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
title One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
spellingShingle One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
Moscoso Londoño, Oscar
Oxides
Chemical Synthesis
Mossbauer Spectroscopy
Xafs (Exafs And Xanes)
title_short One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
title_full One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
title_fullStr One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
title_full_unstemmed One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
title_sort One-step room temperature synthesis of very small g-Fe2O3 nanoparticles
dc.creator.none.fl_str_mv Moscoso Londoño, Oscar
Carrião Dos Santos, Marcus
Cosio Castañeda, C.
Bilovol, Vitaliy
Martinez Sanchez, R.
Lede, Eduardo Javier
Socolovsky, Leandro Martin
Martinez Garcia, Ricardo
author Moscoso Londoño, Oscar
author_facet Moscoso Londoño, Oscar
Carrião Dos Santos, Marcus
Cosio Castañeda, C.
Bilovol, Vitaliy
Martinez Sanchez, R.
Lede, Eduardo Javier
Socolovsky, Leandro Martin
Martinez Garcia, Ricardo
author_role author
author2 Carrião Dos Santos, Marcus
Cosio Castañeda, C.
Bilovol, Vitaliy
Martinez Sanchez, R.
Lede, Eduardo Javier
Socolovsky, Leandro Martin
Martinez Garcia, Ricardo
author2_role author
author
author
author
author
author
author
dc.subject.none.fl_str_mv Oxides
Chemical Synthesis
Mossbauer Spectroscopy
Xafs (Exafs And Xanes)
topic Oxides
Chemical Synthesis
Mossbauer Spectroscopy
Xafs (Exafs And Xanes)
purl_subject.fl_str_mv https://purl.org/becyt/ford/2.5
https://purl.org/becyt/ford/2
dc.description.none.fl_txt_mv Very small maghemite nanoparticles (~3 nm) are obtained through a one-step synthesis at room temperature. The fast neutralization reaction of a ferric solution in a basic medium produces an intermediate phase, presumably two-line ferrihydrite, which in oxidizing conditions is transformed to maghemite nanoparticles. The synthesis of maghemite, as final product of the reaction, was characterized by High-Resolution Transmission Electron Microscopy (HR-TEM), X-ray Absorption Fine Structure (XAFS), Mössbauer spectroscopy, and magnetometry. The XAFS technique allowed the analysis of the crystallographic variations into maghemite nanoparticles as a result of modification in its surface/volume ratio. Mössbauer spectroscopy at low temperature (4.2 K) confirms the presence of Fe(III) in tetrahedral and octahedral interstices, in the stoichiometry corresponding to maghemite. The specific magnetization, M vs H (3 K and 300 K, up to 7 T) and temperature dependence of the magnetization (50 Oe by ZFC mode, 2 K < T < 300 K) indicate that maghemite nanoparticles of 3 nm are in superparamagnetic state with a blocking temperature close to 36 K.
Fil: Moscoso Londoño, Oscar. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Carrião Dos Santos, Marcus. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina. Universidade Federal de Goias; Brasil
Fil: Cosio Castañeda, C.. Universidad Nacional Autónoma de México; México. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Bilovol, Vitaliy. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Martinez Sanchez, R.. Universidad de la Habana; Cuba
Fil: Lede, Eduardo Javier. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Socolovsky, Leandro Martin. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
Fil: Martinez Garcia, Ricardo. Consejo Nacional de Investigaciones Científicas y Técnicas. Oficina de Coordinación Administrativa Houssay. Instituto de Tecnologías y Ciencias de la Ingeniería; Argentina
description Very small maghemite nanoparticles (~3 nm) are obtained through a one-step synthesis at room temperature. The fast neutralization reaction of a ferric solution in a basic medium produces an intermediate phase, presumably two-line ferrihydrite, which in oxidizing conditions is transformed to maghemite nanoparticles. The synthesis of maghemite, as final product of the reaction, was characterized by High-Resolution Transmission Electron Microscopy (HR-TEM), X-ray Absorption Fine Structure (XAFS), Mössbauer spectroscopy, and magnetometry. The XAFS technique allowed the analysis of the crystallographic variations into maghemite nanoparticles as a result of modification in its surface/volume ratio. Mössbauer spectroscopy at low temperature (4.2 K) confirms the presence of Fe(III) in tetrahedral and octahedral interstices, in the stoichiometry corresponding to maghemite. The specific magnetization, M vs H (3 K and 300 K, up to 7 T) and temperature dependence of the magnetization (50 Oe by ZFC mode, 2 K < T < 300 K) indicate that maghemite nanoparticles of 3 nm are in superparamagnetic state with a blocking temperature close to 36 K.
publishDate 2013
dc.date.none.fl_str_mv 2013-05
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/6565
Moscoso Londoño, Oscar; Carrião Dos Santos, Marcus; Cosio Castañeda, C.; Bilovol, Vitaliy; Martinez Sanchez, R.; et al.; One-step room temperature synthesis of very small g-Fe2O3 nanoparticles; Elsevier; Materials Research Bulletin; 48; 5-2013; 3474-3478
0025-5408
url http://hdl.handle.net/11336/6565
identifier_str_mv Moscoso Londoño, Oscar; Carrião Dos Santos, Marcus; Cosio Castañeda, C.; Bilovol, Vitaliy; Martinez Sanchez, R.; et al.; One-step room temperature synthesis of very small g-Fe2O3 nanoparticles; Elsevier; Materials Research Bulletin; 48; 5-2013; 3474-3478
0025-5408
dc.language.none.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://www.sciencedirect.com/science/article/pii/S0025540813004078
info:eu-repo/semantics/altIdentifier/doi/10.1016/j.materresbull.2013.05.042
info:eu-repo/semantics/altIdentifier/doi/
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-nd/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
application/pdf
application/pdf
dc.publisher.none.fl_str_mv Elsevier
publisher.none.fl_str_mv Elsevier
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1846781795429777408
score 12.982451

Publicaciones similares