Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid

Autores
Tasca, Julia Elena; Quincoces, Claudia Edith; Alvarez, Ana María; Gónzalez, María Gloria; Lavat, Araceli Elisabet
Año de publicación
2009
Idioma
español castellano
Tipo de recurso
artículo
Estado
versión publicada
Descripción
In this paper, the effect of the support on the catalytic behavior of CuFe2O4 mixed oxides, supported on ZSM-5 and Al2O3, for a ferrite/support relation of 30%, is analyzed. The supported Cu ferrite was obtained by impregnation of the supports with Cu and Fe nitrates solutions and adding citric acid, for calcination temperatures between 150 and 700ºC. The propane combustion 70 J. E. Tasca et al. was used as reaction test. The catalytic activity was determined in a fixed bed flow reactor at programmed temperature, with a flow of 100 cm3 /min containing a mixture of oxygen 4% and propane 1000 ppm. The addition of 500 ppm of NO in the feed resulted in different effects in the reaction. The zeolitic catalysts demonstrated to be active for the reduction of NO to N2, as well as for the oxidation of propane to CO2. The ferrite supported on Al2O3 only showed activity for the propane oxidation to CO2. For both materials, the propane conversion, in presence of NO in the feed, is shifted towards lower temperatures suggesting that the hydrocarbon activation is modified by the presence of NO.
En este trabajo se analiza el efecto del soporte sobre el comportamiento catalítico de óxidos mixtos de CuFe2O4 soportados sobre ZSM-5 y Al2O3 para una relación ferrita/ soporte igual al 30%. La ferrita de Cu soportada fue obtenida por impregnación de los soportes con solución de nitratos de Cu y Fe, adicionando ácido cítrico, para temperaturas finales de síntesis entre 150 y 700o C. La combustión de propano, fue empleada como reacción test. La actividad catalítica se determinó a temperatura programada en un reactor de flujo a lecho fijo con un caudal de 100 cm3 /min conteniendo una mezcla de 4% de oxígeno y 1000 ppm de propano. El agregado de 500 ppm de NO en la alimentación produjo diferentes efectos en la reacción. Los catalizadores zeolíticos mostraron ser activos para la reducción de NO a N2 y la oxidación de propano a CO2. Las muestras soportadas sobre Al2O3 sólo presentaron actividad para la oxidación del propano a CO2. Ambos materiales muestran que la conversión de propano en presencia de NO en la alimentación se desplaza hacia menores temperaturas sugiriendo que la activación del hidrocarburo es modificada por la presencia de NO.
Fil: Tasca, Julia Elena. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ingenieria Olavarria; Argentina
Fil: Quincoces, Claudia Edith. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Alvarez, Ana María. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Gónzalez, María Gloria. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Lavat, Araceli Elisabet. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ingenieria Olavarria; Argentina
Materia
Cu ferrite
propane combustion
supported mixed oxides
Nivel de accesibilidad
acceso abierto
Condiciones de uso
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
Repositorio
CONICET Digital (CONICET)
Institución
Consejo Nacional de Investigaciones Científicas y Técnicas
OAI Identificador
oai:ri.conicet.gov.ar:11336/23212
Acceder
id CONICETDig_08bde725d21d370c501d8182430d9051
oai_identifier_str oai:ri.conicet.gov.ar:11336/23212
network_acronym_str CONICETDig
repository_id_str 3498
network_name_str CONICET Digital (CONICET)
spelling Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solidTasca, Julia ElenaQuincoces, Claudia EdithAlvarez, Ana MaríaGónzalez, María GloriaLavat, Araceli ElisabetCu ferritepropane combustionsupported mixed oxideshttps://purl.org/becyt/ford/1.4https://purl.org/becyt/ford/1In this paper, the effect of the support on the catalytic behavior of CuFe2O4 mixed oxides, supported on ZSM-5 and Al2O3, for a ferrite/support relation of 30%, is analyzed. The supported Cu ferrite was obtained by impregnation of the supports with Cu and Fe nitrates solutions and adding citric acid, for calcination temperatures between 150 and 700ºC. The propane combustion 70 J. E. Tasca et al. was used as reaction test. The catalytic activity was determined in a fixed bed flow reactor at programmed temperature, with a flow of 100 cm3 /min containing a mixture of oxygen 4% and propane 1000 ppm. The addition of 500 ppm of NO in the feed resulted in different effects in the reaction. The zeolitic catalysts demonstrated to be active for the reduction of NO to N2, as well as for the oxidation of propane to CO2. The ferrite supported on Al2O3 only showed activity for the propane oxidation to CO2. For both materials, the propane conversion, in presence of NO in the feed, is shifted towards lower temperatures suggesting that the hydrocarbon activation is modified by the presence of NO.En este trabajo se analiza el efecto del soporte sobre el comportamiento catalítico de óxidos mixtos de CuFe2O4 soportados sobre ZSM-5 y Al2O3 para una relación ferrita/ soporte igual al 30%. La ferrita de Cu soportada fue obtenida por impregnación de los soportes con solución de nitratos de Cu y Fe, adicionando ácido cítrico, para temperaturas finales de síntesis entre 150 y 700o C. La combustión de propano, fue empleada como reacción test. La actividad catalítica se determinó a temperatura programada en un reactor de flujo a lecho fijo con un caudal de 100 cm3 /min conteniendo una mezcla de 4% de oxígeno y 1000 ppm de propano. El agregado de 500 ppm de NO en la alimentación produjo diferentes efectos en la reacción. Los catalizadores zeolíticos mostraron ser activos para la reducción de NO a N2 y la oxidación de propano a CO2. Las muestras soportadas sobre Al2O3 sólo presentaron actividad para la oxidación del propano a CO2. Ambos materiales muestran que la conversión de propano en presencia de NO en la alimentación se desplaza hacia menores temperaturas sugiriendo que la activación del hidrocarburo es modificada por la presencia de NO.Fil: Tasca, Julia Elena. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ingenieria Olavarria; ArgentinaFil: Quincoces, Claudia Edith. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Alvarez, Ana María. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Gónzalez, María Gloria. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; ArgentinaFil: Lavat, Araceli Elisabet. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ingenieria Olavarria; ArgentinaAsociación Química Argentina2009-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionhttp://purl.org/coar/resource_type/c_6501info:ar-repo/semantics/articuloapplication/pdfapplication/pdfhttp://hdl.handle.net/11336/23212Tasca, Julia Elena; Quincoces, Claudia Edith; Alvarez, Ana María; Gónzalez, María Gloria; Lavat, Araceli Elisabet; Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid; Asociación Química Argentina; Journal of the Argentine Chemical Society; 97; 1; 1-2009; 69-790365-0375CONICET DigitalCONICETspainfo:eu-repo/semantics/altIdentifier/url/http://aqa.org.ar/index.php/volumenes-publicados/51-vol-97-1-january-june-2009info:eu-repo/semantics/openAccesshttps://creativecommons.org/licenses/by-nc-sa/2.5/ar/reponame:CONICET Digital (CONICET)instname:Consejo Nacional de Investigaciones Científicas y Técnicas2025-09-29T09:37:09Zoai:ri.conicet.gov.ar:11336/23212instacron:CONICETInstitucionalhttp://ri.conicet.gov.ar/Organismo científico-tecnológicoNo correspondehttp://ri.conicet.gov.ar/oai/requestdasensio@conicet.gov.ar; lcarlino@conicet.gov.arArgentinaNo correspondeNo correspondeNo correspondeopendoar:34982025-09-29 09:37:09.575CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicasfalse
dc.title.none.fl_str_mv Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
title Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
spellingShingle Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
Tasca, Julia Elena
Cu ferrite
propane combustion
supported mixed oxides
title_short Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
title_full Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
title_fullStr Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
title_full_unstemmed Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
title_sort Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid
dc.creator.none.fl_str_mv Tasca, Julia Elena
Quincoces, Claudia Edith
Alvarez, Ana María
Gónzalez, María Gloria
Lavat, Araceli Elisabet
author Tasca, Julia Elena
author_facet Tasca, Julia Elena
Quincoces, Claudia Edith
Alvarez, Ana María
Gónzalez, María Gloria
Lavat, Araceli Elisabet
author_role author
author2 Quincoces, Claudia Edith
Alvarez, Ana María
Gónzalez, María Gloria
Lavat, Araceli Elisabet
author2_role author
author
author
author
dc.subject.none.fl_str_mv Cu ferrite
propane combustion
supported mixed oxides
topic Cu ferrite
propane combustion
supported mixed oxides
purl_subject.fl_str_mv https://purl.org/becyt/ford/1.4
https://purl.org/becyt/ford/1
dc.description.none.fl_txt_mv In this paper, the effect of the support on the catalytic behavior of CuFe2O4 mixed oxides, supported on ZSM-5 and Al2O3, for a ferrite/support relation of 30%, is analyzed. The supported Cu ferrite was obtained by impregnation of the supports with Cu and Fe nitrates solutions and adding citric acid, for calcination temperatures between 150 and 700ºC. The propane combustion 70 J. E. Tasca et al. was used as reaction test. The catalytic activity was determined in a fixed bed flow reactor at programmed temperature, with a flow of 100 cm3 /min containing a mixture of oxygen 4% and propane 1000 ppm. The addition of 500 ppm of NO in the feed resulted in different effects in the reaction. The zeolitic catalysts demonstrated to be active for the reduction of NO to N2, as well as for the oxidation of propane to CO2. The ferrite supported on Al2O3 only showed activity for the propane oxidation to CO2. For both materials, the propane conversion, in presence of NO in the feed, is shifted towards lower temperatures suggesting that the hydrocarbon activation is modified by the presence of NO.
En este trabajo se analiza el efecto del soporte sobre el comportamiento catalítico de óxidos mixtos de CuFe2O4 soportados sobre ZSM-5 y Al2O3 para una relación ferrita/ soporte igual al 30%. La ferrita de Cu soportada fue obtenida por impregnación de los soportes con solución de nitratos de Cu y Fe, adicionando ácido cítrico, para temperaturas finales de síntesis entre 150 y 700o C. La combustión de propano, fue empleada como reacción test. La actividad catalítica se determinó a temperatura programada en un reactor de flujo a lecho fijo con un caudal de 100 cm3 /min conteniendo una mezcla de 4% de oxígeno y 1000 ppm de propano. El agregado de 500 ppm de NO en la alimentación produjo diferentes efectos en la reacción. Los catalizadores zeolíticos mostraron ser activos para la reducción de NO a N2 y la oxidación de propano a CO2. Las muestras soportadas sobre Al2O3 sólo presentaron actividad para la oxidación del propano a CO2. Ambos materiales muestran que la conversión de propano en presencia de NO en la alimentación se desplaza hacia menores temperaturas sugiriendo que la activación del hidrocarburo es modificada por la presencia de NO.
Fil: Tasca, Julia Elena. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ingenieria Olavarria; Argentina
Fil: Quincoces, Claudia Edith. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Alvarez, Ana María. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Gónzalez, María Gloria. Consejo Nacional de Investigaciones Científicas y Técnicas. Centro Científico Tecnológico Conicet - La Plata. Centro de Investigación y Desarrollo en Ciencias Aplicadas "Dr. Jorge J. Ronco". Universidad Nacional de la Plata. Facultad de Ciencias Exactas. Centro de Investigación y Desarrollo en Ciencias Aplicadas; Argentina
Fil: Lavat, Araceli Elisabet. Universidad Nacional del Centro de la Provincia de Buenos Aires. Facultad de Ingenieria Olavarria; Argentina
description In this paper, the effect of the support on the catalytic behavior of CuFe2O4 mixed oxides, supported on ZSM-5 and Al2O3, for a ferrite/support relation of 30%, is analyzed. The supported Cu ferrite was obtained by impregnation of the supports with Cu and Fe nitrates solutions and adding citric acid, for calcination temperatures between 150 and 700ºC. The propane combustion 70 J. E. Tasca et al. was used as reaction test. The catalytic activity was determined in a fixed bed flow reactor at programmed temperature, with a flow of 100 cm3 /min containing a mixture of oxygen 4% and propane 1000 ppm. The addition of 500 ppm of NO in the feed resulted in different effects in the reaction. The zeolitic catalysts demonstrated to be active for the reduction of NO to N2, as well as for the oxidation of propane to CO2. The ferrite supported on Al2O3 only showed activity for the propane oxidation to CO2. For both materials, the propane conversion, in presence of NO in the feed, is shifted towards lower temperatures suggesting that the hydrocarbon activation is modified by the presence of NO.
publishDate 2009
dc.date.none.fl_str_mv 2009-01
dc.type.none.fl_str_mv info:eu-repo/semantics/article
info:eu-repo/semantics/publishedVersion
http://purl.org/coar/resource_type/c_6501
info:ar-repo/semantics/articulo
format article
status_str publishedVersion
dc.identifier.none.fl_str_mv http://hdl.handle.net/11336/23212
Tasca, Julia Elena; Quincoces, Claudia Edith; Alvarez, Ana María; Gónzalez, María Gloria; Lavat, Araceli Elisabet; Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid; Asociación Química Argentina; Journal of the Argentine Chemical Society; 97; 1; 1-2009; 69-79
0365-0375
CONICET Digital
CONICET
url http://hdl.handle.net/11336/23212
identifier_str_mv Tasca, Julia Elena; Quincoces, Claudia Edith; Alvarez, Ana María; Gónzalez, María Gloria; Lavat, Araceli Elisabet; Preparation and characterization of an AB2O4 spinel type oxide: catalytic application of the supported CuFe2O4 solid; Asociación Química Argentina; Journal of the Argentine Chemical Society; 97; 1; 1-2009; 69-79
0365-0375
CONICET Digital
CONICET
dc.language.none.fl_str_mv spa
language spa
dc.relation.none.fl_str_mv info:eu-repo/semantics/altIdentifier/url/http://aqa.org.ar/index.php/volumenes-publicados/51-vol-97-1-january-june-2009
dc.rights.none.fl_str_mv info:eu-repo/semantics/openAccess
https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
eu_rights_str_mv openAccess
rights_invalid_str_mv https://creativecommons.org/licenses/by-nc-sa/2.5/ar/
dc.format.none.fl_str_mv application/pdf
application/pdf
dc.publisher.none.fl_str_mv Asociación Química Argentina
publisher.none.fl_str_mv Asociación Química Argentina
dc.source.none.fl_str_mv reponame:CONICET Digital (CONICET)
instname:Consejo Nacional de Investigaciones Científicas y Técnicas
reponame_str CONICET Digital (CONICET)
collection CONICET Digital (CONICET)
instname_str Consejo Nacional de Investigaciones Científicas y Técnicas
repository.name.fl_str_mv CONICET Digital (CONICET) - Consejo Nacional de Investigaciones Científicas y Técnicas
repository.mail.fl_str_mv dasensio@conicet.gov.ar; lcarlino@conicet.gov.ar
_version_ 1844613169876566016
score 13.070432

Publicaciones similares